Microstructure and Mechanical Properties of As-cast Mg-5Sn-4Zn-xSi Alloys

Yongqing Tang,Chunming Wang

DOI: https://doi.org/10.15980/j.tzzz.2017.07.004

2017-01-01

Abstract:The microstructure of the as-cast Mg-5Sn-4Zn alloy with 0.5％,1.0％,1.5％ and 2.5％ Si additions was observed by XRD (X-ray diffraction),SEM (scanning electron microscopy).The results reveal that besides of α-Mg and Mg2 Sn phase,Mg2 Si with the Chinese script shape can be observed in the Si containing alloys.Zn exists in the Mg2Sn and Mg2 Si phase or dissolves in α-Mg matrix.Grain size in the alloy can be refined with increasing in Si content,and amounts of Mg2Si are increased.The tensile test at the ambient temperature reveals that the Si addition can result in the deterioration of the tensile properties.The compressive creep behavior of the Mg-Sn-Zn-Si alloy at 175 ℃ with loading of 55 MPa was also investigated.The results reveal that the Si addition is helpful for improving the compressive creep resistance of Mg-Sn-Zn alloy.