Effects of P and La Modification on Silicon Phase in Hypereutectic Al-Si Alloy

Hongfa Wu,Hefa Cheng,Xiaoxiong Qin,Tong Xu,Jun Zhang

DOI: https://doi.org/10.15980/j.tzzz.2017.09.029

2017-01-01

Abstract:The hypereutectic Al-20Si alloys were modified by P and rare earth element La,and effects of P and La on the modification of primary silicon phase in the alloys were investigated.The experimental results indicate that the addition of P can refine greatly primary silicon phase in hypereutectic Al-20Si alloy.The primary silicon phase in modified alloys is changed into fine granule from coarse block shape in unmodified alloys and well-distributed in matrix.The optimal refinement on the primary silicon phase can be obtained when the content of P is 0.06 ％,where the average size of primary silicon phase is decreased from 122 μm to 25μm.However,with the addition of 0.09％ P,the primary silicon in the alloy can be coarsened.The complex modification of P-La can further improve the refining effect of primary silicon.The optimal refinement on eutectic silicon in the alloy can be observed when the content of La is 0.9 ％,while with La of 1.2 ％,over-modification effects can be observed.