Abstract:The hole defects can easily occur in magnesium alloy castings that are prepared by low pressure lost foam casting (LP-LFC) process when the process parameters such as vacuum, pouring temperature and filling velocity are not properly selected. In this study, the forming mechanism of the hole defects in AZ91D magnesium castings by LP-LFC process was investigated. The shape, location and surface appearance of the hole defects were observed using optical microscopy and scanning electron microscopy, and the chemical composition on the surface of the holes was analyzed using energy spectrometer. The result indicates that there are two types of hole defects, i.e., the pyrolysis products related hole defects, including concentrative hole and blow hole defects, and slag related hole defects. The concentrative hole and the blow-hole defects were formed either by the liquid-EPS degradation products entrapped in the molten metal under the condition that the pouring temperature is equal to or lower than 730 ℃, or by the hindered transport of EPS pyrolysis products. Some irregular shape hole defects were caused by slag or by coating slough entrapment when the pouring temperature is equal to 750 ℃ and the filling velocity is equal to or greater than 100 mm·s-1. To reduce or eliminate the hole defects, the vacuum and filling velocity must be properly chosen to ensure that the metal front profile exhibits convex shape and in laminar current state, and the pouring temperature should be just high enough to ensure that the molten melt has adequate heat energy to complete the foam pyrolysis and to fully occupy the mould. For AZ91D magnesium castings in this study, the parameters should be 730 ℃ pouring temperature, 0.02-0.03 MPa vacuum and 80 mm·s-1 filling velocity.

Study on Polystyrene Pattern Loss Process in Mg-alloy EPC

Experimental Study on the Filling Process of the Lost Foam Casting Process of a Cast Iron Plate

Thermal Analysis During Solidification of Mg-4%.wtAl Alloy During Lost Foam Casting Process

Study on the Cavity Defects of Low-Pressure Lost Foam Casting for Magnesium Alloy

Study on Typical Hole Defects in Az91d Magnesium Alloy Prepared by Low Pressure Lost Foam Casting

Porosity of aluminum alloy in lost foam casting process

Determination of casting parameters of thick wall die-casting of magnesium alloy and simulation of its processing

Numerical Simulation and the Application for Filling Process of Expendable Polystyrene Beads in Lost-foam Casting

A benchmark experiment of the mold filling of a cast iron plate by lost foam casting

Three-Dimensional Simulation of EPS Evaporation Process for Lost Foam Casting

Study on the EPC AZ91 magnesium alloy

Mesostructural Design and Manufacturing of Open-Pore Metal Foams by Investment Casting

Effect of Vacuum Degree on Quality of Magnesium Alloy by Low-Pressure Expendable Pattern Casting

Aluminum Foam Sandwich: Pore Evolution Mechanism Investigation and Engineering Preparing Optimization

Numerical Simulation of Filling and Solidification Processes for Magnesium Alloy in Low Pressure Cast Process

Influence of foam pattern density on the surface roughness of expendable pattern-shell compound casting

Investigation of Properties in Magnesium Alloy Thin Plates after Die Casting Processes

Evaluation of the effect of vacuum on mold filling in the magnesium EPC process

Investigation of Microstructures and Mechanical Properties of A356 Aluminum Alloy Produced by Expendable Pattern Shell Casting Process with Vacuum and Low Pressure

Improving Metal Flow in Lost Foam Casting Through Use of Low Thermal Degradation Hot Melt Adhesives

Numerical Simulation of Filling process of Heat Resistant Mg-RE Alloy Piston in Permanent Mold Casting