Abstract:TC4 titanium alloy wire arc additive manufacturing (WAAM) is easy to produce coarse columnar β grain structure which affects mechanical properties. So in this paper, an innovative process of interpass milling assisted TC4 titanium alloy gas tungsten arc welding (GTAW) WAAM is proposed. The controlling interpass milling depth is used to improve the microstructure and mechanical properties of TC4 titanium alloy parts during the GTAW-WAAM. The results showed that the coarse columnar β grains and fine α phase were observed in the non-interpass milling part. When the interpass milling assistance GTAW-WAAM was employed, the coarse columnar β grains transformed into short columnar and equiaxed grains. With the increased of interpass milling depth, the average size of α phase was gradually refined to 13.5 μm below. The highest average microhardness in the top, middle and bottom areas obtained by using the interpass milling depth of 300 μm were 369 HV 0.2 , 371 HV 0.2 and 371 HV 0.2 respectively, which was increased by 32 HV 0.2 , 28 HV 0.2 and 26 HV 0.2 compared with non-interpass milling respectively. The horizontal and vertical ultimate tensile strength first increases and then decreases with the increase of interpass milling depth, reaching its maximum at a milling depth of 300 μm. The highest tensile strength of the horizontal and vertical directions obtained by using the interpass milling depth of 300 μm were 1022 MPa and 1042 MPa. The level of the ultimate tensile strength is related to the combined proportion of total average β grain size and total average <15 μm α phase size, and the proportion of both is balanced and maximized to obtain the maximum ultimate tensile strength. The interpass milling depth of 300 μm satisfies both conditions, so its maximum horizontal and vertical ultimate tensile strength is achieved. Fracture type of tensile specimen was ductile fracture due to observing a lot of dimples on the fracture morphology. The above conclusions show that interpass milling is an aided process to effectively improve the microstructure and mechanical properties of TC4 titanium alloy GTAW wire arc additive manufacturing thin-walled parts, which has high research significance and practical value.

Preparation of Large Size TC4 Alloy Slab

Strengthening of Ti-6al-4v Alloy Forgings

Preparation Process and Phase Transformation of Al-5Ti-0.25C Master Alloy Adopting Ti Machining Chips

Microstructure and fatigue properties of TC4 titanium alloy treated by α+β forging process

Fatigue property and failure mechanism of TC4 titanium alloy in the HCF and VHCF region considering different forging processes

Microstructure and properties of TC25 titanium alloy forged rings

Microstructure and mechanical properties of TC4 titanium alloy hollow shaft formed by cross wedge rolling

Diffusion Welding for TC4 Titanium Alloy/T2 Copper with Vanadium Foil

Formation of Structure and Properties of Two-Phase Ti-6Al-4V Alloy during Cold Metal Transfer Additive Deposition with Interpass Forging

Relationship among Forging Technology, Structure and Properties of Tc21 Alloy Bars

Numerical simulation study on solidification process of titanium slab ingot by electron beam cold hearth melting

Processing map of titanium alloy TC4 and its application for plate rolling analyses

Experimental study and numerical simulation of α lamellar globularization for TC21 titanium alloy during multidirectional forging

Study on Preparation Process and Properties of CVD Tungsten Composite Coating on TC4 Titanium Alloy Surface

Influence of Heat Treatment on the Microstructure and Mechanical Properties of TC4 Alloy Fabricated by Selective Laser Melting

Microstructure and Mechanical Properties of An Ultrahigh-strength Titanium alloy Ti-4.5Al-5Mo-5V-6Cr-1Nb Prepared Using Laser Directed Energy Deposition and Forging: A Comparative Study

Mechanism of Preparing Laminar Composite Using Ti-Based Amorphous Alloy

The microstructures and mechanical properties of the TC4 titanium alloy fabricated by laser composite manufacturing technology

Comparative study on micro-milling machinability of titanium alloys prepared by different processes: Forging process, additive manufacturing process and heat-treatment process

Improvement of Microstructure and Mechanical Properties of TC4 Titanium Alloy GTAW based Wire Arc Additive Manufacturing by using Interpass Milling

Tailoring Ultrafine Grained and Dispersion-Strengthened Ti2AlC/TiAl Composite Via a New Fabrication Route