Effect of pH Value on Ni-Cr-Mo Alloy Coating Prepared by Pulse Electroplating

Haipeng LIU,Zhitong ZHANG,Xinyue WANG,Qingbo MENG,Yungang LI,Haili YANG
DOI: https://doi.org/10.14158/j.cnki.1001-3814.2017.18.035
2017-01-01
Abstract:Ni-Cr-Mo alloy coatings were prepared on the surface of Q235 steel by pulse electroplating meth. The effects of pHvalue on the element content, deposition rate, surface morphology and corrosion resistance of the coating were investigated by glow discharge spectroscopy (GDS), scanning electron microscopy (SEM), Tafel curve and electrochemical impedance spectroscopy (EIS). The results show that with the increase of pHvalue, Ni content in the coating decreases firstly and then increases, Cr content increases firstly and then decreases, Mo content decreases. The deposition rate of the coating increases firstly and then decreases; in 3.5 % NaCl solution, the corrosion resistance of the coatings strengthens firstly and then weakens. The coating prepared in 3.5 pHbath is uniform and compact, which has the biggest corrosion potential (-0.535V), the smallest corrosion current density (0.123 μA·cm-2) and the biggest charge transfer resistance (2550 Ω·cm2), then, the coating exhibits the best corrosion resistance.
What problem does this paper attempt to address?