Abstract:Modern micro-alloyed, control-rolled TMCP steels generally have good strength, high toughness, and good weldability. However, these valuable properties come along with certain undesirable features, such as low strain hardening (high yield to tensile ratio), low ductility as measured by uniform elongation (elongation at ultimate tensile strength), and possible heat-affect-zone (HAZ) softening due to reduced hardenability. These undesirable features are particularly detrimental in strain-based design of pipelines. Although the phenomenon of HAZ softening has been known for a long time, the impact of the HAZ softening on the integrity of pipeline girth welds was not well understood. The objective of this work was to understand the impact of HAZ softening on girth weld integrity. Finite element analysis was conducted to investigate the effects of HAZ softening on crack driving force and strain concentration in girth welds under longitudinal tensile loading. The material properties of WM and BM were obtained from an X100 girth weld. The HAZ was modeled as a functionally graded material based on its measured hardness. The models contained surface-breaking defects located at the fusion boundary simulating lack-of-sidewall fusion defects. The analysis results showed that increased CTOD driving force can be expected due to HAZ softening. The extent of increase is positively related to the width and degree of softening of the HAZ. On the other hand, weld strength overmatch reduces the total CTOD driving force. The strain concentration in the softened HAZ circumferentially remote from a surface-breaking defect was small. However, high strain concentration existed over the circumference covering the length of the defect. This concentration was primarily attributable to the existence of the defect and secondarily to the HAZ softening. One significant result from this work was that the relative increase in CTOD driving force and strain concentration due to HAZ softening was independent of defect size. In other words, on a relative basis, HAZ softening was no worse on large defects than on smaller defects. This result should be helpful in rationalizing the effects of HAZ softening for defects of various sizes that exist in field applications. Non-symmetrical crack-tip deformation occurred with softened HAZ. A large proportion of the crack-tip deformation was located in the HAZ. The magnitude of non-symmetric deformation increased with the increase of HAZ width and degree of softening. Even higher degree of non-symmetric deformation occurred with the increase of weld overmatching level. The structural significance of reduced total CTOD driving force and increased un-symmetric deformation at the crack tip due to weld strength overmatch warrants further study. The reduction in total CTOD driving force alone does not necessarily results in a higher level of weld integrity if the “intrinsic” toughness of the HAZ is substantially lower than the weld metal.

Study on Softening in HAZ and Its Influence on Welded Joints of X70 Pipeline Steel

Significance of Haz Softening on Strain Concentration and Crack Driving Force in Pipeline Girth Welds

Microstructure Transformation of Coarse-Grained Region in Heat-Affected Zone During Welding of Ultra-Low Carbon Ultra-High Strength Pipeline Steel

Effect of V Content and Heat Input on HAZ Softening of Deep-Sea Pipeline Steel

Research on Microstructure and Performance in Welding HAZ of X100 SAWH Pipe

Microstructure Transformation of X70 Pipeline Steel Welding Heat-Affected Zone

Experiment on the Fracture Toughness of Weld Joint of X70 Pipeline Steel

Cracking Reasons of X70 Steel Submerged Arc Weld Pipe during Guide-Bend Test

Effect of H2S Corrosion on the Fracture Toughness of the X80 Pipeline Steel Welded Joint

Effect of Microstructure on Mechanical Properties of X65MS Welded Pipe Joint

Effect of softening of 6082-T6 aluminum alloy CMT welded joints on mechanical properties and fracture behavior

Coarse Grain Heat Affect Zone Microstructures and Toughness of X80 Pipeline Steel

Research on Hydrogen-Induced Induced Cracking Sensitivity of X80 Pipeline Steel under Different Heat Treatments

Effects of welding heat input on structure and properties of 800 MPa ultra fine grained steel welding joints

Effect of root welding heat input on microstructure evolution and fracture mechanism in intercritically reheat-coarse grained heat-affected zone of X80 pipeline steel

Fracture driving forces of cracked girth welds with mechanical heterogeneity for X80 pipes

Effect of microstructure on hydrogen embrittlement and hydrogen-induced cracking behaviour of a high-strength pipeline steel weldment

Strength calculation and microstructure characterization of HAZ softening area in 6082-T6 aluminum alloy CMT welded joints

Study on the mechanical properties of X80 pipeline steel under pre-charged high-pressure gaseous hydrogen

Stress-Corrosion-Cracking Sensitivity of the Sub-Zones in X80 Steel Welded Joints at Different Potentials

Microstructure and Property of Coarse Grain Haz X80 Pipeline Steel