Abstract:<p>A circumferential crack in the fusion line is a major threat to the structural integrity of the pipeline girth weld because it may possibly lead to fracture failure when subjected to large plastic deformations. For the newly constructed X80 pipeline with an outside diameter (OD) of 1422 mm in China, the complicated configuration of welded joints and the outer diameter are outside the range of the general fracture assessment standards, such as BS 7910. Furthermore, during the pipe manufacture process, pipeline designers merely specify the minimum yield strength limit according to the pipe steel grade. This results in a wide variation range in the choice of yield strength values of the base metal. This also leads to a serious problem in the fracture assessment of pipe girth weld because the weld strength is commonly considered to be either evenly matched or overmatched. The foregoing factors make it difficult to perform an accurate fracture assessment using conventional standards. This study therefore aims to investigate the fracture behavior of 1422-mm OD pipelines with a double-V groove weld and circumferential crack in the fusion line. The specific effect of material mismatch and the realistic operational parameters that influence the fracture capacity of the pipe are examined via a series of numerical investigations. First, a rigorous three-dimensional finite element model to simulate the pipe girth weld is established by utilizing the ABAQUS finite element code package. The weld, which has a canoe-shaped surface crack in the fusion line between the heat-affected zone and root welding metal, is subjected to biaxial loading conditions. The keyhole method is adopted to simulate the crack front as well as the crack tip to eliminate the stress singularity effect during deformation. A refined mesh strategy is introduced to ensure the accurate simulation of the stress and strain fields in the vicinity of the crack tip. Based on the numerical model, the J-integral fracture parameter, which is clearly defined based on a strict mechanical theory, is chosen to characterize the effect of strength matching ratio, internal pressure, and yield to tensile strength ratio on the crack driving force. A new strain-based J-integral prediction formula is proposed based on numerical results.</p>

Safe Assessment of Offshore Pipeline under Weld Mismatched Condition Based on Different Standards

Fracture and Fatigue Assessment on Submarine Pipelines with Crack Damages

Safety Test Research of Pressure Pipes Containing Incomplete Welding Defects

Research On Safety Assessment Method For Pressure Pipe With Incomplete Welding Defects Under Complicated Loadings

Pressure test method of safety assessment on existed submarine pipeline

Safety Evaluation and Defect Analysis on Oil Pipeline

Buckling Response of Offshore Pipelines under Combined Tension and Bending

Submarine Transportation Pipeline Safety Assessment System and Its Application

Safety assessment of incomplete penetration defects at the root of girth welds in pipelines

Mismatch effect on safety assessment of pressure pipe with incomplete penetration defect

On Collapse Failure Analysis Of Subsea Corroded Sandwich Pipelines Under External Pressure

Fracture analysis of X80 welded joints with variable wall thickness and misalignment

A Tiered Approach to Girth Weld Defect Acceptance Criteria for Stress-Based Design of Pipelines

Evaluating Fitness-for-Service of Corroded Metal Pipelines: Structural Reliability Bases

Configuration Analysis of Deepwater S-Lay Pipeline

Study on safety evaluation method of incomplete penetration welded pipeline under combined loads of internal pressure and bending moment

Data-driven probabilistic failure assessment curve based on similitude principle

Quantitative research on stress failure risk assessment for girth welds with unequal wall thickness of the X80 pipeline under lateral load

Study of Strain Capacity for High-Strain Marine Pipe

Fracture response of 1422-mm diameter pipe with double-V groove weld joints and circumferential crack in fusion line

Failure Analysis and Fitness-for-service Assessment for a Pipeline