Cold Extrusion of Metal Plastic Forming Process on Metal Flow Lines and Grain Structure Impacts of Electro-hydraulic Vibration Applied in

Yang Qinghua,Hong Xiaoxiao,Wang Zhiheng,Bao Guanjun,Hu Xinhua,Xue Junyi

DOI: https://doi.org/10.3969/j.issn.1004-132X.2015.16.017

2015-01-01

Abstract:Cold extrusion process had some disadvantages,such as gigantic metal deformation re-sistance,mold wear,etc.a new type of cold extrusion process was proposed,where vibration excitation signals were applied in the cold extrusion process.Using DEFORM-3D finite element analysis soft-ware,the system simulation models were built and the forming process was simulated on whether the vibration was applied to this process.Simulation results show that the signal can be applied to facili-tate the metal flow,and the metal flow rate reaches 62.4 mm/s.The degree of deformation of the mesh flow lines is smaller than that in the condition of traditional squeeze mode.A kind of electro-hy-draulic vibration experimental platform and die were designed for this project.Experiments were com-pleted on the conditions of whether the vibration was applied to this process.Etching molded parts with 4% Nital,and SEM was used to observe the part sections.Experimental results show that after the application of vibration signals in cold extrusion,the grain size reduce from about 3.3 ~5.0μm to 1.7 ~3.3 μm,grain deformation becomes more uniform,deformation tissue becomes more dense,me-tallic fibrous tissue becomes finer and longer.