Abstract:Highly ordered TiO2 nanotube array electrodes were successfully fabricated by a two-step anodization method on Ti sheet substrates in an electrolyte composed of ammonium fluoride, deionized water, and glycol. The tube wall was smooth, and the average internal and external diameters, wall thickness, and tube length achieved were 80 nm, 90 nm, 10 nm, and 9 μm, respectively. X-ray diffraction and field emission scanning electron microscopy results revealed that the TiO2 nanotube arrays presented an amorphous structure. When calcined at 300 °C, the arrays crystallized into the anatase phase, and the crystallization degree of the oxide layer increased as the temperature rose. Calcinating at 400 °C did not obviously disrupt the porous structure of the highly ordered arrays. However, higher temperature enlarged the diameter of the nanotube array and roughened the tube wall. When the temperature reached 600 °C, the nanotube mouth broke because of the excessive stress, causing the oxide layer’s thinness and nanotube mouth clogging. The photoelectric test showed that the electrode presented obvious photoresponse under 300–400 nm UV excitation (maximized at 360 nm). The degree of crystallization and the micro-structure of the oxide layer can significantly affect the photoelectric properties of the electrode. After calcination at 400 °C, the TiO2 nanotube arrays, with highly ordered tubular structure directly connected to the Ti substrate, can ensure the rapid transportation of photo-induced electrons to the Ti substrate, while the high crystallinity of the arrays can help reduce the defect density of the nanotube and extend the lifetime of the photo-induced carriers. The electrode showed the best photoelectric property, and the photocurrent intensity was maximized (29.6 μA). However, the calcination process with over-temperature resulted in substantial loss of the TiO2 oxide layer, mouth clogging, and a severe decline in the photoelectric properties.

Preparation and Photoelectric Performances of 3D Net Structure TiO2 Nano-Tubes

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Synthesis and Photoelectrochemical Properties of Self-Organized Anodic TiO2 Nanotube Arrays

Solvothermal Growth of Three-Dimensional TiO2 Nanostructures and Their Optical and Photocatalytic Properties

Preparation of High Efficient Photoelectrode of N–F-codoped TiO2 Nanotubes

Preparation and Enhanced Photoelectrocatalytic Properties of a Three-Dimensional TiO2-Au Porous Structure Fabricated Using Superaligned Carbon Nanotube Films

Optimization of Cds/Tio2 Nanotube-Array Composite Photocatalysts Prepared by Electrodeposition

Synthesis and Photoelectrochemical Properties of Self-Organized Anodic TiO<sub>2</sub> Nanotube Arrays

Preparation and Photoelectric Performance of ZnO/TiO_2 Nanocomposites

TiO2 Nanotubes with Tunable Morphology, Diameter, and Length: Synthesis and Photo-Electrical/Catalytic Performance

Preparation of TiO2 Nanotube Photocatalyst by Anodization and Improvement of Photocatalytic Performance

Preparation and characterization of visible-light-sensitive anodic Cu-Ti-O nanotube arrays

Study on Fabrication and UV Photoelectric Property of TiO2 Nanotube Array Electrodes.

Fabrication and Field Emission Characteristics of TiO2 Nano-Tube Arrays

Fabrication and characterization of photoelectrocatalytic electrodes of carbon nanotube/titanium oxide

TiO2 nanotube arrays prepared by anodic oxidation method

Investigation on the Photoelectrocatalytic Activity of Well-Aligned Tio2 Nanotube Arrays

Preparation and Photocatalytic Properties of V-doped TiO_2 Nanotube Arrays

Controllable Synthesis of Well-Ordered TiO2 Nanotubes in a Mixed Organic Electrolyte for High-Efficiency Photocatalysis

Photoelectrochemical properties of nano-TiO2 film electrodes prepared by thermal oxidation