Abstract:Highly ordered TiO2 nanotube array electrodes were successfully fabricated by a two-step anodization method on Ti sheet substrates in an electrolyte composed of ammonium fluoride, deionized water, and glycol. The tube wall was smooth, and the average internal and external diameters, wall thickness, and tube length achieved were 80 nm, 90 nm, 10 nm, and 9 μm, respectively. X-ray diffraction and field emission scanning electron microscopy results revealed that the TiO2 nanotube arrays presented an amorphous structure. When calcined at 300 °C, the arrays crystallized into the anatase phase, and the crystallization degree of the oxide layer increased as the temperature rose. Calcinating at 400 °C did not obviously disrupt the porous structure of the highly ordered arrays. However, higher temperature enlarged the diameter of the nanotube array and roughened the tube wall. When the temperature reached 600 °C, the nanotube mouth broke because of the excessive stress, causing the oxide layer’s thinness and nanotube mouth clogging. The photoelectric test showed that the electrode presented obvious photoresponse under 300–400 nm UV excitation (maximized at 360 nm). The degree of crystallization and the micro-structure of the oxide layer can significantly affect the photoelectric properties of the electrode. After calcination at 400 °C, the TiO2 nanotube arrays, with highly ordered tubular structure directly connected to the Ti substrate, can ensure the rapid transportation of photo-induced electrons to the Ti substrate, while the high crystallinity of the arrays can help reduce the defect density of the nanotube and extend the lifetime of the photo-induced carriers. The electrode showed the best photoelectric property, and the photocurrent intensity was maximized (29.6 μA). However, the calcination process with over-temperature resulted in substantial loss of the TiO2 oxide layer, mouth clogging, and a severe decline in the photoelectric properties.

Preparation and Photocatalytic Properties of V-doped TiO_2 Nanotube Arrays

Fabrication of Well-Aligned Tio2 Nanotube Arrays with Outstanding Light-Induced Hydrophilicity Performance

Preparation and Photocatalytic Activities of TiO2 Nanotubes with Mixed Crystal Structure

Temperature-dependent differences in wettability and photocatalysis of TiO 2 nanotube arrays thin films

Preparation and Photoelectrocatalytic Performance of TiO<sub>2</sub> Nano-Tubes Arrays Electrode

Preparation and Photoelectrocatalytic Performance of TiO2 Nano-Tubes Arrays Electrode

Study on Fabrication and UV Photoelectric Property of TiO2 Nanotube Array Electrodes.

Boron-doped TiO2 Nanotube Array: in Situ Electrochemical Preparation and Study on Its Photocatalytic Activity

Facile Synthesis of Ni-doped TiO2ultrathin Nanobelt Arrays with Enhanced Photocatalytic Performance

Study on preparation of TiO_2 nanotube arrays by anodizing processes

Investigation on the Photoelectrocatalytic Activity of Well-Aligned Tio2 Nanotube Arrays

Research on Cu-doped TiO_2 Nanotube Arrays

Enhancement of Visible-Light-Induced Photocurrent and Photocatalytic Activity of V and N Codoped TiO2 Nanotube Array Films

Preparation and photoelectric performanceof high-aspect-ratio TiO 2 nanotube arrays film electrode

Facile Fabrication, Characterization, and Enhanced Photoelectrocatalytic Degradation Performance of Highly Oriented Tio2 Nanotube Arrays

Preparation and Photocatalytic Activity of Vanadium-doped Nano-TiO_2

Fabrication of carbon-modified TiO2 nanotube arrays and their photocatalytic activity

Enhanced Photoelectrochemical Properties of Ta-TiO2 Nanotube Arrays Prepared by Magnetron Sputtering

Synthesis of carbon-modified TiO2 nanotube arrays for enhancing the photocatalytic activity under the visible light

Study on Synthesis in Situ and Photocatalytic Activity of Tio2 Nanotubes Array Films

Fabrication and formation mechanism of self-organized TiO2 nanotube arrays