In Situ Synchrotron X-Ray Diffraction Studies of the Phase Transitions in LiNi0.5Mn1.5O4 Cathode Materials
Jing-Kun Li,Wen,Yu-Shi He,Zi-Feng Ma
DOI: https://doi.org/10.1149/ma2011-02/7/397
2011-01-01
ECS Meeting Abstracts
Abstract:The LiNi0.5Mn1.5O4 spinel is one of the most promising cathode materials for high power lithium ion batteries because of its good electrochemical performance and high operating voltage around 4.7 V [1]. Recently, most studies have focused on the development of synthesis routes since the manufacturing method for LiNi0.5Mn1.5O4 powder strongly influences its rate performance and capacity retention. Many synthesis methods, such as the improved solid-state reaction [2-3], hydrothermal synthesis [4], coprecipitation [5], molten salt synthesis [6], ultrasonic spray pyrolysis [7] and combinational annealing [8], were developed. The LiNi0.5Mn1.5O4 structure with a space group of Fd3m can be changed to P4332 by the annealing process, which readily makes the oxidation state of Mn change from +3 to +4, leading to the perfect LiNi0.5Mn1.5O4 crystal structure. Sun et al. [9] reported that the LiNi0.5Mn1.5O4cathode with the space group of Fd3m showed better electrochemical behaviors than did the LiNi0.5Mn1.5O4 cathode with the space group of P4332, and the ex situ XRD patterns showed that stoichiometric LiNi0.5Mn1.5O4 (P4332) had an intermediate phase of Fd3hm during Li extraction. The chemical states and structure changes accompanying the electrochemical Li deintercalation of Li(Mn,M)2O4 (M=Ni, Co, Cr) 5V cathode materials were studied by Terada et al [10] using in situ X-ray absorption fine structure (XAFS) technique. Herein, we reported in situ synchrotron XRD studies of the phase transitions in LiNi0.5Mn1.5O4 cathode materials during cycling. The LiNi0.5Mn1.5O4 powder was prepared by spray drying and post-annealing method, the procedure is similar to the literature elsewhere [8]. Stoichiometric amounts of CH3COOLi·2H2O, Ni(CH3COO)2·4H2O, and Mn(CH3COO)2⋅4H2O (2:1:3) were thoroughly solved in distilled water and mixed using spray drying. Mixed precursors were annealed at 550 and 900 °C with temperature programmed control process. In situ XRD spectra were collected on beam line BL14B1 at the Shanghai Synchrotron Radiation Facility at an energy of 4000~22000 eV (λ=1.2398 A). The Li/LiNi0.5Mn1.5O4 cell was charge-discharged continuously during XRD pattern collection. In situ XRD patterns of LiNi0.5Mn1.5O4 cathode materials during charge from 3.5 to 5.0 V were shown in Figure 1. It can be seen that all of the Bragg peaks refer to the pristine cubic phase was shifted to the higher angle as lithium ion was deintercalated from the LiNi0.5Mn1.5O4 host materials (the voltage increased from bottom to top XRD pattern). There are seven Bragg peaks, (111), (311), (400), (331), (511), (440) and (531), were recorded from each 2θ scan. The (111), (311) and (331) peaks began to broaden when the cell was charged to above 4.75 V, and the (400) and (511) peaks were split into two peaks, respectively. Moreover, the (440) and (531) peaks began to merge together and separate again at the fully charged state. It indicated that new phases were formed when the charge state was above 4.75 V. Figure 2 shows the In situ XRD patterns transition of the (311) peak during the first charge-discharge at a C/10 rate. We can found that the typical (311) peak shift back to the lower angle after the cell was discharged to 3.5 V, but the 2θ value refer to the (311) peak is a little bit bigger than those of before charge. It could be concluded that the structure change of cathode material can be recovered after cycling, and the lattice face distance become narrow. More data will be presented in detail lately. Acknowledgement The authors are grateful for the financial support of this work by the National Basic Research Program of China (2007CB209705). References 1. R Santhanam, B Rambabu, J. Power Sources, 195, 5442 (2010). 2. Chen Z Y, Zhu H L, Ji S, Linkov V, Zhang J L, Zhu W, J. Power Sources, 189, 507 (2009) 3. Lin C Y, Duh J G, Hsu C H, Chen J M, Mater. Lett., 64, 2328 (2010). 4. Huang X K, Zhang Q S , Gan J L , Chang H T, Yang, Y, J. Electrochem. Soc., 158, A139 (2011). 5. Fan Y K, Wang J M, Ye X B, Zhang, J Q , Mater. Chem. Phys., 103, 19 (2007). 6. Kim J H, Myung S T, Sun Y K, Electrochim. Acta, 49, 219 (2004). 7. Park S H, Sun Y K, Electrochim. Acta, 50, 431 (2004). 8. Li D C, Ito A, Kobayakawa K, Noguchi H, Sato Y, Electrochim. Acta, 52, 1919 (2007). 9. Kim J H, Myung S T, Yoon C S, Kang S G, Sun Y K, Chem. Mater., 16, 906 (2004). 10. Terada Y, Yasaka K, Nishikawa F, Konishi T, Yoshio M, Nakai I, J. Solid-State Chem., 156, 286 (2001).