Coordination polymer-reinforced composite polymer electrolyte for all-solid-state Li-metal batteries
Jiaxi yuan,Hao Dong,Bin Wang,Ming Qiu,Zhendong Liu,Xiaojun wu,Sheng Zhong,Gangsheng tong,Zhenying chen,Jichao Zhang,Qing zhang,Jinhui Zhu,Xiaodong Zhuang
DOI: https://doi.org/10.2139/ssrn.4668450
IF: 15.1
2024-03-20
Chemical Engineering Journal
Abstract:Composite polymer electrolytes (CPEs) have garnered significant interest due to their lightweight, flexible, and suitability for large-scale processing. However, current CPEs still face challenges such as unsatisfactory ionic conductivity (σ), low Li + transference number ( t + ), and poor interfacial stability. This study presents the synthesis of a coordination polymer by coordinating Co 2+ with terpyridine-end-capped polyethylene glycol (Co(tpy)-PEG). The resulting Co(tpy)-PEG-reinforced PEO-based CPE exhibits exceptional properties, including a high σ of 0.22 mS cm −1 , large t + of 0.75, and superior durability in both Li|Li (1400 h at 0.2 mA cm −2 ) and Li|LiFePO 4 cells (70% capacity retention after 1000 cycles at 1C) at 60 °C, comparable to the best available CPEs. The incorporation of Co(tpy)-PEG filler plays a vital role in enhancing the σ by disrupting the PEO crystallinity and creating additional Li + conducting pathways. Additionally, it can free Li + to increase t + through Lewis acid-base interactions between Co 2+ and TFSI − /O atoms, as well as NO 3 − and Li + . Furthermore, Co(tpy)-PEG facilitates the formation of a stable multicomponent solid electrolyte interphase containing beneficial Li 2 S x , LiF, and Li 3 N. This work introduces a promising strategy for designing and preparing multifunctional fillers capable of simultaneously reinforcing the σ, t + , and interfacial stability of CPEs.
engineering, chemical, environmental