Effect of Mn2+ substitution on phase composition, microstructure, and microwave dielectric properties of Zn1.8-xMnxSiO3.8 ceramics
Fei Liu,Xiang Guo,Xiang Ding,Tao Que,Huan Wang,Jie Xu,Heng Miao,Hongqing Zhou
DOI: https://doi.org/10.1007/s10854-024-13909-2
2024-12-13
Journal of Materials Science Materials in Electronics
Abstract:Microwave dielectric ceramics are essential for producing microwave components, seriously affecting the development and application of wireless communication technology. In this paper, Zn 1.8- x Mn x SiO 3.8 (0 ≤ x ≤ 0.20) ceramics were prepared by solid-phase reaction method. The sintering characteristics, phase compositions, microstructures, and dielectric properties of the materials were investigated. The addition of Mn 2+ ions lowered the sintering temperature of the ceramics, and the densification temperature decreased from 1300 to 1200 °C as the amount of Mn 2+ substitution increased. The Mn 2+ substitution ( x = 0–0.2) effectively formed a Zn 2 SiO 4 solid solution without the appearance of any other secondary phases. A moderate amount of Mn 2+ improves the microscopic morphology of Zn 1.8- x Mn x SiO 3.8 ceramics and enhances their Q × f . The theoretical and relative densities of the material were maximized at x = 0.04, where the ρ bulk = 4.0865 g/cm 3 and ρ rela = 97.7%. At x > 0.12, the grain size grows, and anomalous grains appear and increase, deteriorating the microwave dielectric properties. The Q × f values are related to the microscopic morphology and packing fraction. α obs increases from 13.360 to 13.596, the same trend as the α theo , suggesting that ε r is mainly affected by the ion polarizability. Among all the samples, the optimum microwave dielectric properties of Zn 1.76 Mn 0.04 SiO 3.8 ceramics were obtained by sintering at 1275 °C for 3 h: ε r = 6.44(at 13.153 GHz), Q × f = 71,175.7 GHz, τ f = − 50.7 ppm/°C. Due to its low dielectric constant and excellent quality factor, it will become the most promising electronic substrate material.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied