Preparation and Structure of Hydrosilated Trans-1,4-Polyisoprene

Meiqin JI,Xin ZHAO,Yingdong ZHANG,Dongmei YUE,Liqun ZHANG

DOI: https://doi.org/10.3969/j.issn.1000-890X.2018.05.011

2018-01-01

Abstract:The preparation and structure of hydrosilated trans-1,4-polyisoprene (HsTPI) were studied.The best hydrosilylation process of trans-1,4-polyisoprene (TPI) was obtained as follows:reaction temperature was 105 ℃,reaction time was 12 h,mass fraction of catalyst relative to TPI was 0.07,and the molar quantities of triethyl silane and vinyl group in TPI were equal.1H-NMR and Si-NMR were carried out to confirm that triethyl silicane group was grafted into TPI C-C main molecular chain.Thermogravimetric analysis showed that the decomposition temperature of HsTPI gradually increased along with degree of hydrosilation increasing,and the thermal mass loss of HsTPI changed from one-stage decomposition to two-stage decomposition.DSC test result showed that the glass-transition temperature of HsTPI increased along with degree of hydrosilation increasing.X-ray diffraction analysis showed that with the increase of the degree of hydrosilation,the crystal form of HsTPI changed and the crystallization ability was weakened.The mechanical properties of HsTPI deteriorated with the increase of hydrosilation degree.