Preparation of Triblock Copolymers with High &ITCis&IT-1,4-polybutadiene as Soft Segments

Lu Dai,Qin-zhuo Zhou,Bo-geng Li,Su-yun Jie
DOI: https://doi.org/10.11777/j.issn1000-3304.2017.17052
2017-01-01
Acta Polymerica Sinica
Abstract:Taking high cis-1,4 hydroxyl-terminated polybutadiene (HTPB) as a starting material, two kinds of triblock copolymers were successfully synthesized by polymerization of epsilon-caprolactone (epsilon-CL) and styrene. Polycaprolactone-b-polybutadiene-b-polycaprolactone triblock copolymer (CLBCL) was synthesized via the ring-opening polymerization of epsilon-CL with stannous octanoate [Sn(Oct)(2)] as the catalyst and HTPB as the macroinitiator. The length of PCL segments was controlled by changing the reaction time based on the living property of the ring-opening polymerization. Besides, the reaction between HTPB and 2-bromoisobutyryl bromide yielded the Atom Transfer Radical Polymerization (ATRP) macroinitiator (BiB-PB-BiB), which was used for the preparation of the polystyrene-b-polybutadiene-b-polystyrenetriblock copolymers (SBS) via the Activators Regenerated by Electron Transfer for ATRP (ARGET ATRP) of styrene. The ARGET ATRP reaction was controllable and the molecular weight distribution of the copolymers was narrow. The structure of these triblock copolymers was characterized by Fourier transform infrared spectroscopy (FTIR), nuclear magnetic resonance spectroscopy (H-1-NMR and C-13-NMR), gel permeation chromatography (GPC), and their thermal properties were tested by thermo gravimetric analysis (TGA) and differential scanning calorimetry (DSC). TGA analysis indicated that the thermal stability of the CLBCL triblock copolymers increased with the increase in PCL content in the copolymers. Only one thermal degradation stage was observed for the SBS triblock copolymers from the TGA curves and the thermal stability of copolymers was slightly better than HTPB precursors. In the DSC curves of CLBCL copolymers, the glass transition temperature at -106.0 degrees C for the PB segments and the melting temperature at 54.4 degrees C for the PCL segments were detected. The results of DSC analysis for the SBS triblock copolymers indicated that there were two glass transition temperatures at -104.1 and 102.4 degrees C, which corresponded to the PB and the PS segments, respectively.
What problem does this paper attempt to address?