Abstract:Lithium acrylate (LiAA) was in situ prepared in nitrile rubber (NBR) through neutralization of lithium hydroxide (LiOH) and acrylic acid (AA) during mixing. The NBR/LiAA compounds were vulcanized with dicumyl peroxide (DCP). The in situ preparation and polymerization of LiAA were characterized using Fourier transform infrared (FTIR) spectrometer. The micrographs of the compounds and vulcanizates were explored using a scanning electron microscope (SEM). The effects of DCP and LiAA contents on the water-swelling and mechanical properties of the vulcanizates were studied. The relationship between the LiOH/AA molar ratio and the properties of the vulcanizates was investigated. The results showed that the in situ formed LiAA could improve the mechanical properties and water–swelling properties of the NBR/LiAA vulcanizates. The vulcanizates properly compounded had high water-swelling ratio over 800% and tensile strength more than 12MPa. The differential scanning calorimetry (DSC) measurements indicated that the water absorbed in the vulcanizate existed in PLiAA and NBR networks in three different physical states, namely, free water, freezable bound water and non-freezable bound water.

Study on Water-Swelling Rubber with CPE Modified by in Situ Formed Acrylate

A new approach to preparation of water-swelling rubber

Water‐swelling Elastomer Prepared by in Situ Formed Lithium Acrylate in Chlorinated Polyethylene

Preparation and Properties of A Water-Swelling Rubber by in Situ Formed Lithium Acrylate in Nitrile Rubber

Water-swelling Property of In-Situ Formed PNaAA/EPDM

Investigation of modified NBR with in-situ polymerization of lithium acrylate and its water absorption properties

"Preparation and Water-Swelling Properties of Grafted Natural Rubber Based Water-Swellable Rubber"

Modification of Polyethylene by in Situ Formed Sodium Acrylate

Water swelling rubber prepared by in situ formed sodium acrylate in EVM

Study On The Synthesis And Properties Of Water Soluble Superplasticizer With Side Branch Poly(Ethylene Glycol) Methyl Ether

The role of dicumyl peroxide in the preparation of chloroprene rubber/starch/sodium acrylate water-swellable composites

Mechanical properties, water swelling behavior, and morphology of swellable rubber compatibilized by PVA-g-PBA

Preparation and Properties of in Situ Polymerization of Poly (vinyl Chloride)

Ethylene-propylene-diene rubber filled with nano-calcium carbonate in-situ modified by methacrylic acid Ⅰ.Effect of curing agent and methacrylic acid amount

Synthesis and Characterization of Self-cross Linking Hybrid Silicone-acrylate Emulsion at Ambient Temperature

Study of Dielectric Properties of Crosslinked LLDPE Modified by In-situ Polymerization

Synthesis and characterization of acrylic rubber

Deproteinized Natural Rubber‐graft‐polyacrylamide‐graft‐polystyrene (dpnr‐g‐pam‐g‐pst): Preparation and Performance Study of a New Water Swellable Rubber

A Study on the Grafting Modified Water-Absorbent Resin by Microwave Irradiation and Its Blending

Preparation and Characterization of Composites: Epdm-G-Aa/Caco3

Reinforcement of Elastomers by in Situ Prepared Aluminum Methacrylate