Abstract:Abstract Nylon-6 and acrylate rubber (ACM) were melt blended in a Brabender Plasticorder at 220 °C and 40 rpm rotor speed. The reactive nature of the blend is reflected in the mixing torque behavior of the blends at different compositions. The solubility characteristics of the blends in formic acid solution gives an approximate idea of the amount of nylon-6 grafted onto ACM and vice-versa. A reaction mechanism is proposed based on the well known epoxy—amine and epoxy—acid reactions and is confirmed by infrared spectroscopic studies of the blends. The influence of interaction between the two polymers on the mechanical and the dynamic mechanical properties of the blends is analyzed in detail, and the results are interpreted on the basis of the formation of nylon—ACM graft copolymer at the interfaces. The dynamic mechanical thermal analysis (DMTA) reveals a two phase morphological structure, indicating incompatibility of the blend components. The grafting reaction results in dramatic increase in both the storage modulus and the Young's modulus of blends. The presence of grafted rubber chains is reflected in the secondary transition of the rubber loss peak at higher temperature. Also, a substantial improvement in the damping properties of the blends in the service temperature range (i.e., 25 to 175 °C) is revealed from the DMTA results. The dynamic vulcanization of the ACM phase during melt mixing improves the elongation at break values of the blends.

Synthesis and characterization of acrylic rubber

Influence of Small Amount of Co-Monomers on Acrylonitrile Polymerization in Dimethylformamide (DMF) Solution

The Molecular Structure Control of Butyl Methacrylate/acrylamide (Co)polymers

Synthesis and Characterization of Self-cross Linking Hybrid Silicone-acrylate Emulsion at Ambient Temperature

Synthesis and Performance of A Self Crosslinkable Acrylate Copolymer with High Compatibility for an Oil Well Cement Modifier

Investigation of Preparation of Acrylate Rubber with Solution Polymerization

Characterization of chemical structure and morphology of MCS graft terpolymer

Structure and Property of Epoxy-Functionalized Acrylic Rubber Toughened Polylactide

Study on Damping Properties of Acrylate Latex Copolymer

New Chemistries and Technologies Derived from a Common Reaction of Α‐methylstyrene at 61 °C

Synthesis, characterization, and pressure-sensitive properties of butyl acrylate and methyl acrylate copolymers

Preparation and Properties of Silicone-Acrylate Copolymer Latex

Studies on the continuous precipitation copolymerization of acrylonitrile in aqueous medium with high monomer feed concentration: I conversion, MW and MWD

Preparation of low‐temperature self‐crosslinking acrylic resin and its performance research

Thermoplastic Elastomeric Blends of Nylon-6/Acrylate Rubber: Influence of Interaction on Mechanical and Dynamic Mechanical Thermal Properties

Synthesis and Characterization of Heat‐resistant N‐phenylmaleimide–styrene–maleic Anhydride Copolymers and Application in Acrylonitrile–butadiene–styrene Resin

A STUDY ON POLYMERIZATION OF AN ACRYLIC MONOMER\=HAVING DIKETONIC MOIETY

Synthesis of Low Polymerization Degree PVAc and the Rheologic Features of Reaction Liquid

Synthesis and Surface Characterization of Poly(methyl Methacrylate)‐block‐polydimethylsiloxane Copolymers from Macroazoinitiator

Synthesis And Characterization Of The Polyacrylongtrlle-Blockpoly(Methyl Acrylate) By Raft Technique

Synthesis and Polymerization of Gamma-Alkoxy-Beta-Hydroxypropyl Acrylates