Effect of Organosilane-modified Polycarboxylate-Superplasticizer on Fluidity and Hydration Process of Cement Paste

Yan HE,Xiong ZHANG,Mingdong GU,Wanling HONG
DOI: https://doi.org/10.14062/j.issn.0454-5648.2016.08.13
2016-01-01
Abstract:A series of organosilane-modified polycarboxylate superplasticizers were synthesized via the radical polymerization in aqueous solution, in which acylic acid (AA) was partially or completely substituted by 3-(trimethoxysilyl) propyl methacrylate. This work mainly investigated the adsorption, dispersing performance of these polymers and their effect on cement hydration. The results show that partially-silylated polycarboxylates exhibit higher adsorption amount than reference polycarboxylate, while fully-silylated polycarboxylate shows a reduced adsorption amount. Partially-silylated polycarboxylate can improve the dispersing properties of cement paste, but the addition of excessive amount results in the decrease of fluidity. The flow retainability of partially-silylated polycarboxylates is lower than that of reference polycarboxylate, and the viscosity and the yield stress increase more steeply. Although partially-silylated polycarboxylate leads to a prolonged induction period, after the induction period, the accelerated hydration degree at 3 d occurs by adding partially-silylated polycarboxylate into cement paste. The fully-silylated polycarboxylate results in the enhanced prolonging induction period without acceleration in hydration degree at 3 d or 28 d hydration ages.
What problem does this paper attempt to address?