Abstract:This study investigates how different sodium silicate SiO2/Na2O MS ratios (0.75, 0.9, and 1.2) affect the hydration behavior of amorphous wollastonitic hydraulic (AWH) binders containing various amounts of Al2O3 content (4, 7, 10, and 12%wt). The effects of and interaction between the MS ratio of the activator and the Al2O3 content of the sample on the hydration reaction and paste performance were investigated. The reaction was followed by calorimetry, and the pastes' compressive strength performances were tested at different curing times (2, 7, and 28 days). The hydrated pastes were characterized by FTIR, thermogravimetry analysis, and X-ray diffraction. The calorimetric results show that a higher Al2O3 cContent and a higher MS ratio result in a longer induction period. In terms of paste performance, an increase of the Al2O3 coupled with an activation with a 1.2 MS ratio results in a lower compressive strength after 28 days of hydration; the results range from 76 to 52 MPa. A decrease of the MS ratio to 0.9 allowed the obtention of a narrower range of results, from 76 to 69 MPa. Even though a decrease of the MS ratio to 0.75 led to higher hydration kinetics and high compressive strength results at early ages, at 28 days of curing, a decrease in compressive strength was observed. This may be a consequence of the fast kinetic of the mixture, since the rapid growth of hydration products may inhibit the dissolution at later ages and increase the porosity of the paste. Moreover, the high Al intake in the hydration product, facilitated by the high sodium content of the activator, promotes the formation of a higher number of calcium aluminate silicate hydrate structures (C-A-S-H) to the detriment of calcium silicate hydrate structures (C-S-H), decreasing the compressive strength of the samples. The TGA results indicate that the samples hydrated with the MS075 solution resulted in a higher number of hydrated products at early ages, while the samples hydrated with the MS09 and MS1.2 solutions exhibit a steady increase with curing time. Hence, an equilibrium in the hydration kinetic promoted by Si saturation-undersaturation appears to be fundamental in this system, which is influenced by both the MS ratio and the Al(OH)4- content in solution. The results of this study suggest that for this type of binder, optimal performance can be achieved by decreasing the MS ratio to 0.9. This composition allows for a controlled kinetic and overall higher compressive strength results in pastes produced with this AWH precursor.

The Influence of Silanes on Hydration and Strength Development of Cementitious Systems

Influence of silane on hydration characteristics and mechanical properties of cement paste

Evaluation of Admixture Silane Added into Cementitious Pastes

Study on alkylsilane-incorporated cement composites: Hydration mechanism and mechanical properties effects

Study on the Influence of Nanosilica Sol on the Hydration Process of Different Kinds of Cement and Mortar Properties

The use of tetraethyl orthosilicate silane (TEOS) for surface-treatment of hardened cement-based materials: A comparison study with normal treatment agents

Effect of Lithium Silicate Composite Sol on the Properties of Concrete Surface

The Influence of Superabsorbent Polymers and Nanosilica on the Hydration Process and Microstructure of Cementitious Mixtures

Performance of Silane -Based Surface Treatments for Protecting Degraded Historic Concrete

Internal hydrophobic treatment for mortar containing supplementary cementitious materials: thermal analysis of kinetics and products of hydration

Influence of nano-silica agglomeration on microstructure and properties of the hardened cement-based materials

INVESTIGATING THE EFFECT OF NANO SILICA ON THE MECHANICAL PROPERTIES OF HARDENED CEMENT PASTE

Effect and mechanism of colloidal silica sol on properties and microstructure of the hardened cement-based materials as compared to nano-silica powder with agglomerates in micron-scale

Effect of the specific surface area of nano-silica particle on the properties of cement paste

Research on the influence of property of composite cement mortar to silane coupling agents

Physicochemical effects of nanosilica on C 3 A/C 3 S hydration

Relationship Between Microscopic Pore Structure and Strength of Cement-Based Materials with Low Water-Binder Ratio Under Sulfate Attack Environment

Influence of Silica Modulus on the Activation of Amorphous Wollastonitic Hydraulic Binders with Different Alumina Content: Study of Hydration Reaction and Paste Performance

Interaction of Silylated Superplasticizers with Cementitious Materials

Comparative Study of Effect of Raw and Densified Silica Fume in the Paste, Mortar and Concrete

Influence of silane treatment on the freeze-thaw resistance of concrete