Study on Surface Modification of Glass Fiber by Starch Nanocrystals

Qin Nie,Yuanxi Chen,Yao Chang,Xiaodong Zhou
DOI: https://doi.org/10.3969/j.issn.1001-3539.2017.06.023
2017-01-01
Abstract:The glass fiber was treated with starch nanocrystals (SNC) prepared by self to increase the interface shear strength (IFSS) with epoxy resin matrix. The influences of treatment methods,treatment time,concentration of SNC ethanol dispersion solu-tion and heat treatment temperature on the surface deposition of SNC and the interfacial properties of the modified glass fiber and epoxy resin were studied. The fibers before and after treatment were characterized by scanning electron microscopy and single fiber strength tester,and the interface bonding of the fiber and epoxy resin was analyzed by using microdebonding method. The results show that SNC can be deposited on the surface of glass fiber uniformly,when the fiber is deposited by gravity standing for 24 h and the concentration of SNC ethanol dispersion solution is 1 g/100 mL,the IFSS is increased obviously,to 27.29 MPa,improved by 29.3% compared with the untreated fiber. After heat treatment at 150℃ for 4 h,X-ray photoelectron spectroscopy shows there ex-ists chemical bonds between glass fiber and SNC and improves the interface bonding of the fiber and epoxy resin further,the IFSS reaches 32.30 MPa,is improved by 53% compared with the untreated fiber,and the tensile strength of the fiber can be well kept.
What problem does this paper attempt to address?