High tensile strength glass fiber with different ratios of Na 2 O and SiO 2 prepared by chemical strengthening method

Chuanxiang Sun,Shengyun Yang,Lulu Zhang,Yi Cao,Ya Qu,Yunlong Yue,Junfeng Kang

DOI: https://doi.org/10.1016/j.jnoncrysol.2023.122621

IF: 4.458

2023-09-22

Journal of Non-Crystalline Solids

Abstract:In this paper, chemical strengthening method was used to prepare high strength glass fiber with different Na 2 O/SiO 2 molar ratios (N/S). The structure, viscosity and tensile strength of glass samples were investigated by Molecular dynamics (MD) simulation, Raman, rotational viscometer and tensile strength tests. Results showed that the variation trends of Q n units obtained by MD simulation and Raman spectra were consistent, both indicating the decrease of the degree of network polymerization (DNP) with N/S ratio increasing. Additionally, the DNP had excellent linear relationships with the glass forming temperature and tensile strength of fresh glass fiber, respectively. However, the tensile strength was significant improved after chemical strengthening. When N/S ratio increased or chemical strengthening time prolonged, the enhancement rate of tensile strength of treated glass fiber was increased. The optimal tensile strength of glass fiber was 3089.38 ± 7 MPa after chemical strengthening at 390 °C for 30 min with N/S ratio 0.17.

materials science, multidisciplinary, ceramics