Abstract:The reactive extrusion of maleic anhydride grafted polypropylene (PP-g-MAH) with ethylenediamine (EDA) as coupling agent was carried out in a co-rotating twin-screw extruder to produce long chain branched polypropylene (LCBPP). Part of PP-g-MAH was replaced by maleic anhydride grafted high-density polyethylene (HDPE-g-MAH) or linear low-density polyethylene (LLDPE-g-MAH) to obtain hybrid long chain branched (LCB) polymers. Compared with the linear PP, PE and their blends, the LCB polyolefins exhibit excellent dynamic shear and transient extensional rheological characteristics such as increased dynamic modulus, higher low-frequency complex viscosity, significantly enhanced melt strength and strain-hardening behaviors. LCB polymers also have higher tensile strength, tensile modulus, impact strength and lower elongation at break than linear polymer and their blends. Supercritical carbon dioxide (scCO2) was introduced in the reactive extrusion process. With the presence of scCO 2, the motor current of twin extruder was decreased and LCB polyolefins with lower MFR, higher complex viscosity and increased tensile strength and modulus were obtained. This indicates that the application of scCO2 can reduce the viscosity of melt in extruder, enhance the diffusion of reactive species, facilitate the reaction between functional groups, and increase the LCB density. The foaming behavior of both linear and LCB polyolefins were studied. The results show that cellular materials produced from the LCB polyolefins have higher weight reduction, smaller cell size and better mechanical properties than those produced from the linear polymers.

PreparationProcess of PP Grafted with Acrylic Acid Modiifed Layered Double Hydroxide

Simultaneous Graft Polymerization of Polypropylene with Maleic Anhydride and Butyl Acrylate

Study on Melt-Grafting of Maleic Anhydride Onto Polypropylene in the Presence of Styrene

Study on Solid Phase Grafting of Acrylic Acid onto Polypropylene to Prepare Hydrophilic Polypropylene

Supercritical Carbon Dioxide-Assisted Preparation of Polypropylene Grafted Acrylic Acid with High Grafted Content and Small Gel Percent

Preparation of Long Chain Branched Pp Via Multi-Monomer Melt Grafting in the Presence of Bi-Functional Monomer 1,6-Hexanediol Diacrylate

Melt Grafting Of A Long-Chain Unsaturated Carboxylic Acid Onto Polypropylene

Preparation of high melt strength polypropylene by the reactive extrusion process and its foaming application

New Insight into the Action of Supercritical Carbon Dioxide for Grafting of Maleic Anhydride Onto Isotactic Polypropylene by Reactive Extrusion

Preparation of toughened polypropylene-g-poly (butyl acrylate-Co-acrylated castor oil) by suspension grafting polymerization

The Study of Melt Grafting Mechanism of Acrylic Acid and Butyl Acrylate Onto Low Density Polyethylene and Its Application As Internal Plasticizer

Nondegradative Melt Functionalization of Polypropylene with Glycidyl Methacrylate

Study on the Graft Reaction of Poly(propylene) Fiber with Acrylic Acid

The Effect Of Feed Composition Of Styrene And Acrylic Acid On The Properties Of Modified Low Density Polyethylene

Photo-grafting Poly(acrylic Acid) Onto Poly(lactic Acid) Chains in Solution

A Facile Approach to Modify Polypropylene Flakes Combining O2-plasma Treatment and Graft Polymerization of L-lactic Acid

Graft Modification of Chlorinated Polypropylene and Coating Performance Promotion for Polypropylene

Study of Melt Free Radical Grafting of Maleic Anhydride and Styrene Onto Polypropylene and Its Properties

Synthesis of multifunctional polypropylene via solid phase cografting and its grafting mechanism

Grafting copolymerization of acrylamides onto preirradiated PP films

Grafting Polymerization of Acrylic Acid Onto Preirradiated Polypropylene Fabric