Influence of coating solutions on properties ofγ-Al2O3 washcoat over FeCrAl substrate

Zhifei ZHANG,Jinghong ZHOU,Guanghua YE,Xinggui ZHOU

DOI: https://doi.org/10.11949/j.issn.0438-1157.20160286

2016-01-01

Abstract:Twoγ-Al2O3 washcoats on FeCrAl substrate were prepared by dip-coating boehmite sol gel orγ-Al2O3 slurry. The effects of coating solution on the washcoat properties were extensively studied. The washcoat morphology, crystal structure, texture and adhesion to substrate were investigated by SEM, XRD, nitrogen physic sorption and ultrasonic vibration. At coating loading less than 3%(mass), boehmite washcoats were crack-free butγ-Al2O3 washcoats were crack-rich. At coating loading above 8%(mass), boehmite washcoats developed crack, flake and delamination whereasγ-Al2O3 washcoats developed only crackings without delamination. In case of requirement for relatively low coating loading (< 8%), boehmite washcoats were more suitable as carrier for monolithic catalysts due to higher specific surface area and pore volume thanγ-Al2O3 washcoats.γ-Al2O3 washcoats were preferred as catalyst carrier if higher coating loading was needed (> 8%).