Study on Silane Crosslinking LLDPE and Its Friction and Wear Performance

Miao Zheng,Heng Lin,Baicun Zheng,Xin Meng

DOI: https://doi.org/10.15925/j.cnki.issn1005-3360.2017.03.005

2017-01-01

Abstract:Silane crosslinking LLDPE was prepared through the water boiling crosslinking method with a melting mixed silane grafted masterbatch and catalyst masterbatch.The effects of catalytic masterbatch dosage,water bath temperature and crosslinking time on the crosslinked LLDPE gel content,mechanical properties,friction and wear properties were studied.The surface morphology of cross-linked samples was characterized by SEM.Furthermore,the wear mechanism was discussed.The results show that the gel content reaches to a maximum value of 73.0％ and the tensile strength is up to 23.3 MPa,when the mixture is boiled at 70℃ for 9 h with 10％ catalyst masterbatch dosage.The wear loss of LLDPE decreases from 25.3g/kg to 0.5g/kg and the friction coefficient increases from 0.62 to 0.70,indicating that the wear-resisting performance is greatly improved.