Abstract:A modified nano-calcium carbonate (R-CCR) was prepared by coating a layer of unsaturated hydroxylfatty acid on the surface of CCR powders using a solid state method; the latter were commercial nano-CaCO 3 modified with stearic acid. FTIR studies indicate that the modifier is combined on the surface of CaCO 3 . PP/EPDM/nano-CaCO 3 ternary composites were prepared by a melt-mixing method. SEM and TEM were utilized to examine the morphology of the composites. The tensile fractured surface of PP/EPDM/R-CCR showed a fibroid morphology and large-scale yield deformation. The impact fractured surface showed that the amount of cavities in the PP/EPDM/R-CCR system was increased, however their size diminished obviously. R-CCR particles were dispersed uniformly in the PP matrix, and their compatibility was distinctly improved as compared to CCR when the amount of R-CCR was 15 h −1 . The tensile strength remained nearly constant (reduced from 27.6 MPa to 27.5 MPa), while the impact strength increased from 9.6 kJ/m 2 to 15.4 kJ/m 2 as CCR was replaced by R-CCR. Meanwhile, the bending strength and bending modulus also increased correspondingly. Furthermore, the impact strength of PP/EPDM/R-CCR was maintained at a high level (15.4 kJ/m 2 ), which was more than the sum of that of PP/EPDM and PP/R-CCR (6.6 kJ/m 2 and 6.1 kJ/m 2 respectively). This indicates that the R-CCR and EPDM have a significant synergistic toughening effect on PP while maintaining the strength and modulus of virgin PP. Both the storage modulus G′ and loss modulus G″ of PP/EPDM and PP/EPDM/R-CCR composites increase with increasing frequency, but the values of G′ and G″ of the tertiary composite are relatively higher than those of the binary system. The loss factor and viscosity decrease with increasing frequency, but there is little difference between tertiary and binary composites. The apparent viscosity η of the tertiary system containing R-CCR is lower than that of the tertiary system containing CCR and virgin PP. The viscosity of the composites sig-nificantly decreases with increasing shear rate. The mea-sured mechanical properties of the composites indicate that replacing CCR with R-CCR for binary composites could simultaneously enhance the toughness and strength of PP.

Study of Dispersants for PP／nano-CaCO3 Blend

Effect of Oleic Acid-modified Nano-CaCO3 on the Crystallization Behavior and Mechanical Properties of Polypropylene

Comb-like copolymer dispersant for PP/CaCO<sub>3</sub> composites: effects of particle concentration on properties of composites

Novel Comb-Like Copolymer Dispersant for Polypropylene/CaCO3 Composites and Its Influence on Dispersion, Crystallization, Mechanical, and Thermal Properties

Comb-Like Copolymer Dispersant for Pp/Caco3 Composites: Effects of Particle Concentration on Properties of Composites

The Influence of Calcium Carbonate on the Mechanical Properties and Phase Morphology of PA6/PP Blend

Preparation and property analysis of polyacrylate dispersant for calcium carbonate

Study on the Properties and Structure of Polypropylene Modified with Nano-Sized CaCO_3

Application of Dispersants in Antistatic PP/CB Composites

Effect of Supercritical Carbon Dioxide-Assisted Nano-Scale Dispersion of Nucleating Agents on the Crystallization Behavior and Properties of Polypropylene

Study On Crystallization Behaviour Of Polypropylene Containing Nano-Calcium Carbonate And Organic Nucleating Agents

Effects of Nanoparticle Treatment on the Crystallization Behavior and Mechanical Properties of Polypropylene/calcium Carbonate Nanocomposites

Nano-meter CaCO_3 Modified by Polyester Type Hyperdispersant and Its Application

Mechanical and Thermal Properties of Polypropylene (PP) Composites Filled with CaCO3 and Shell Waste Derived Bio-Fillers

Effects of Nano Calcium Carbonate Modified by a Lanthanum Compound on the Properties of Polypropylene

EFFECTS OF CaCO3 PARTICLE SIZE AND SIZE DISTRIBUTION ON PROPERTY AND STRUCTURE OF PP

Crystallization Behavior of PP in Composites with EPDM and a Surface Modified Nano-Calcium Carbonate

Effect of Unsaturated Hydroxyl-Fatty Acid Modified Nano-Caco3 on the Morphological and Rheological Behavior of PP

Studies on the Influence of Novel Nano-Activator Titanium Dioxide on the Properties of PP

Effect of Nanoparticle Surface Treatment on Nonisothermal Crystallization Behavior of Polypropylene/Calcium Carbonate Nanocomposites

Effect of Nano-Caco3 on Properties of Pp/Tlcp/Caco3 In-Situ Hybrid Materials