Thermal Regeneration Mechanisms of Mn-Ce/Activated Coke (AC) Catalysts for Low Temperature NOxReduction

Liu YANG,Yue TAN,Zhong-yi SHENG,Ai-yi ZHOU,Yu-feng HU,Yun-xia SHAN

DOI: https://doi.org/10.3969/j.issn.1003-9015.2015.06.022

2015-01-01

Abstract:Mn-Ce/activated coke (AC) catalysts were synthesized via an impregnation method. A fixed bed was used to simulate a moving bed reactor under two stages with desulfurization and denitrification processes, and Mn-Ce/AC catalysts saturated with SO2 were prepared. Nitrogen and water vapor was used to thermally regenerate the catalyst. However, all of the NOx conversions rates were lower than 50%. Brunauer-Emmett-Teller method (BET), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and temperature programmed desorption (TPD) were used to characterize the catalyst and the results show that the surface area and pore volume of the regenerated catalyst decreased significantly, with no recovery of Ce3+ and Lewis acid sites. XPS results show that SO2 reacted with CeO2 to form Ce2(SO4)3 or Ce(SO4)2, which reduced the active centers of Ce and blocked catalyst pores, and reduced NOx conversion rates of the regenerated catalysts.