Abstract:A desirable catalyst for efficiently controlling NOx emissions often demands excellent SO2 poisoning resistance. Here, we introduced Ce to modify birnessite-MnO2 to obtain a Ce-MnO2 catalyst with excellent activity (T90 = 85 °C) for the selective catalytic reduction of NO with NH3 (NH3-SCR) at low temperatures. Compared with the MnO2 catalyst that was severely deactivated after poisoning, the Ce-MnO2 catalyst showed a significant improvement in SO2 resistance with the NO conversion slightly decreasing from 100 to 95% at 150 °C. Physicochemical characterizations combined with density functional theory calculations indicated that the sulfates formed on Mn species and Ce species played different roles in the SCR reaction. The SO32– adsorbed on the surface of the MnO2 catalyst can react with NH3 to form ammonium sulfites, leading to the deactivation of the catalyst. However, the SO42– from Ce2(SO4)3 on the sulfated Ce-MnO2 catalyst existed as new adsorption sites of NH4+, thus providing this catalyst with more acid sites. In addition, SO2 was preferentially adsorbed and oxidized on Ce species, thereby protecting the Mn active centers from sulfation and deactivation. This work reveals the mechanism of Ce in promoting SO2 resistance over birnessite-MnO2 from the perspective of sulfates.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acscatal.0c05697?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acscatal.0c05697</a>.Details of experimental section; summary of the catalytic activity of Mn–Ce catalysts for NH3-SCR at low temperatures reported in the previous literature; NH3-SCR activity and N2 selectivity of fresh catalysts; SEM and TEM images of fresh catalysts; and TG and DTG profiles of the catalysts after poisoning (<a class="ext-link" href="/doi/suppl/10.1021/acscatal.0c05697/suppl_file/cs0c05697_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Graphitic Carbon Nitride (G-C3n4) as a Super Support for Mn-Ce Based Nh3-Scr Catalyst: Improvement of Catalytic Activity and H2o/So2 Tolerance

Graphitic carbon nitride (g-C3N4) as a super support for Mn–Ce based NH3-SCR catalyst: Improvement of catalytic performance and H2O/SO2 tolerance for NO removal

C,N‐modified TiO2‐supported Mn–Ce–Cox‐based Catalyst for Low‐temperature NH3‐SCR

Mnox/Ceo2/Sio2 Catalysts Prepared by Adsorption Phase Reaction Technique for Selective Catalytic Reduction of Nox at Low-Temperature

Catalytic performance of CeO2-NPs and α-MnO2 mixed oxides catalysts for low-temperature NH3-SCR of NO

C,N ‐modified TiO 2 ‐supported Mn–Ce–Co x ‐based catalyst for low‐temperature NH 3 ‐SCR

Mechanistic insight into the promoting effect of partial substitution of Mn by Ce on N2 selectivity of MnTiO catalyst for NH3-SCR of NO

CeO 2 Catalysts for NH 3 ‐ SCR at Low Temperatures

Mechanism and Kinetics Study on Low-Temperature NH3-SCR over Manganese–Cerium Composite Oxide Catalysts

Dual single-atom Ce-Ti/MnO2 catalyst enhances low-temperature NH3-SCR performance with high H2O and SO2 resistance

Enhancing low-temperature NH3-SCR performance of Fe–Mn/CeO2 catalyst by Al2O3 modification

In Situ Supported Mnox-Ceox On Carbon Nanotubes For The Low-Temperature Selective Catalytic Reduction Of No With Nh3

A MnO<sub>2</sub>-based catalyst with H<sub>2</sub>O resistance for NH<sub>3</sub>-SCR: Study of catalytic activity and reactants-H<sub>2</sub>O competitive adsorption

Adjustment of operation temperature window of Mn-Ce oxide catalyst for the selective catalytic reduction of NOx with NH3

"Oxynitride trap" over N/S co-doped graphene-supported catalysts promoting low temperature NH3-SCR performance: Insight into the structure and mechanisms

A highly effective NbMnCeOx catalyst for NH3-SCR and in situ DRIFTS for investigating the reaction mechanism

Mechanistic insights into the influence of preparation methods and Fe3+ doping on the low-temperature performance of MnCeO catalyst for NH3-SCR reaction

Highly Selective Catalytic Reduction of NOx by MnOx–CeO2–Al2O3 Catalysts Prepared by Self-Propagating High-Temperature Synthesis

Mechanism of Ce-Modified Birnessite-MnO 2 in Promoting SO 2 Poisoning Resistance for Low-Temperature NH 3 -SCR

Low-temperature SCR of NO with NH3 over AC/C Supported Manganese-Based Monolithic Catalysts

Comparison of Mn doped CeO2 with different exposed facets for NH3-SCR at low temperature