Abstract:The construction of silicone elastomers crosslinked by a natural crosslinker under a catalyst-free method is highly desirable. Herein we present catalyst-free silicone elastomers (SEs) by simply introducing tannic acid (TA) as a natural crosslinker when using poly (aminopropylmethylsiloxane- co -dimethylsiloxane) (PAPMS) as the base polymer. The crosslinked bonding of these SEs can be easily changed from hydrogen bonding to covalent bonding by altering the curing reaction from room temperature to heating condition. The formability and mechanical properties of the SEs can be tuned by altering various factors, including processing technique, the amount of TA and aminopropyl-terminated polydimethylsiloxane, the molecular weight and -NH 2 content of PAPMS, and the amount of reinforcing filler. The hydrogen bonding was proved by the reversible crosslinking of the elastomers, which can be gradually dissolved in tetrahydrofuran and re-formed after removing the solvent. The covalent bonding was proved by a model reaction of catechol and n -decylamine and occurred through a combination of hydroxylamine reaction and Michael addition reaction. These elastomers exhibit good thermal stability and excellent hydrophobic property and can bond iron sheets to hold the weight of 500 g, indicating their promising as adhesives. These results reveal that TA as a natural product is a suitable “green” crosslinker for the construction of catalyst-free silicone elastomers by a simple crosslinking strategy. Under this strategy, TA and more natural polyphenols could be certainly utilized as crosslinkers to fabricate more organic elastomers by selecting amine-containing polymers and further explore their extensive applications in adhesives, sealants, insulators, sensors, and so forth.

Preparation and characterization of organosilicon tackifier for silicone rubber/copper foil

Studies on Adhesion Performance of Epoxy Resin/Polymercaptan Toughened with Propoxylated Glycerin Triglycidyl Ether

Preparation of Low Temperature Curing Organic Silicone Coating Fabric with Ablation Resistant Property

Synthesis of a siloxane oligomer containing methyl acryloxy group for promoting the adhesion of addition-type silicone rubber to copper plate

The synthesis, characterization and properties of silicone adhesion promoters for addition-cure silicone rubber

Promoters for Improved Adhesion Strength between Addition-Cured Liquid Silicone Rubber and Low-Melting-Point Thermoplastic Polyurethanes

Effect of Silane Coupling Agent on Adhesion Properties between Hydrophobic UV-curable Urethane Acrylate and Acrylic PSA

Effect of graphite and its surface modification on thermal conductivity of silicone rubber

Modification of Fe2O3 and its effect on the heat‐resistance of silicone rubber

Modification of Fe<sub>2</sub>O<sub>3</sub>and its effect on the heat-resistance of silicone rubber

Development of Organosilicon Adhesive with Low Decomposition and High Temperature Resistance

Preparation Of Nanosilica Reinforced Waterborne Silylated Polyether Adhesive With High Shear Strength

Silane modification of semi-curing epoxy surface: High interfacial adhesion for conductive coatings

Synthesis and application of adhesion promoter containing phenolic hydroxyl/acrylate groups for addition-cure liquid silicone rubber

A new organosilicon adhesive based on polysiloxane and polysilazane

EFFECT OF SiO2 NANO-PARTICLES ON ADHESION STRENGTH OF COPPER CONDUCTIVE ADHESIVES

Preparation and Properties of One Component RTV Silicone Resin Composed of Polysiloxane Block Copolymer

Effect of the functional group of silanes on the modification of silica surface and the physical properties of solution styrene-butadiene rubber/silica composites

Preparation of Polyacrylate Emulsion with High Adhesion Properties by Adding Modified Silica Sol

Preparation, characterization, and properties of organic silicone intermediate-modified epoxy resin copolymers

Tannic Acid as a Natural Crosslinker for Catalyst-Free Silicone Elastomers From Hydrogen Bonding to Covalent Bonding