Preparation of polymer/montmorillonite composite water plugging agent
Lin LI,Yi-Jun FAN,Wei HE,Xu WANG
DOI: https://doi.org/10.16606/j.cnki.issn0253-4320.2017.08.031
2017-01-01
Abstract:In order to improve the temperature resistance and salt resistance of water plugging agent,a plugging agent is synthesized through using montmorillonite to modify the polymer that contains 2-acrylanmido-2-methylpropanesulfonic acid (AMPS).The structure of the synthesized polymer is analyzed by infrared spectrometer,SEM and EDS,and its properties such as water absorption rate and sealing rate of the gel are investigated.The optimal synthesis conditions are proposed as that gelling temperature is 60℃,m(AM) ∶m(AA) ∶m(AMPS) =12∶2.5∶4,mass fraction for cross-linking agent is 0.3％,dosage of montmorillonite is 0.5 g (50 mL).The influence ability of various factors on the water absorption rate are as follows:mole ratio of monomer ＞ dosage of cross-linking agent ＞ gelling temperature＞montmorillonite dosage.In the 105 mg·L-1 NaCl solution at 70℃,the composite gel has still maintained the strength Ⅰ after 15 days since it is synthesized,and its thermal stability is stronger than common gel without montmorillonite.The common gel has a better water absorption rate than composite gel,but its heat resistance after absorbing water is weaker than the composite gel.When composite gel has been soaked in 4× 104 mg· L-1 of simulated formation water for 12 h,its water absorption rate reaches the best at 90℃,being 18.29 g· g-1.Besides,it is of great plugging performance.Its plugging rate against matrix core is up to 99.43％,and breakthrough pressure gradient is 123.85 MPa·m-1.