Abstract:TiB2-BN composite ceramics combine excellent electrical conductivity, thermal shock resistance, high-temperature resistance, corrosion resistance, and easy processing of TiB2 and BN. However, in practical applications, their high-temperature oxidation resistance is poor and the resistivity distribution is uneven and changes substantially with temperature. A TiB2-BN-SiC composite ceramic with stable and controllable resistivity was prepared by introducing SiC into the TiB2-BN composite ceramics. In this work, spark plasma sintering (SPS) technology was used to prepare TiB2-BN-SiC composite ceramics with various TiB2-SiC ratios and sintering temperatures. The samples were tested by XRD, SEM, and thermal and mechanical analysis. The results show that as the volume ratio of TiB2-SiC was increased from 3:1 to 12:1, the resistivity of the sample decreased from 8053.3 to 4923.3 μΩ·cm, the thermal conductivity increased from 24.89 to 34.15 W/(m k), and the thermal expansion rate increased from 7.49 (10−6/K) to 10.81 (10−6/K). As the sintering temperature was increased from 1650 to 1950 °C, the density of the sample increased, the mechanical properties were slightly improved, and the resistivity, thermal expansion rate, and thermal conductivity changed substantially. The volume ratio and sintering temperature are the key factors that control the resistivity and thermal characteristics of TiB2-SiC-BN composite ceramics, and the in situ from liquid phases of FeB and FeO also promotes the sintering of the TiB2-BN-SiC ceramics.

The Structure and Mechanical Properties of SiC-TiB2 Multiphase Ceramics Sintered by Spark Plasma Sintering

Influence of Adding TiB2 on Structure and Mechanical Properties of SiC-Based Composite Ceramics

Effect of temperature on the structure and mechanical properties of SiC–TiB2 composite ceramics by solid-phase spark plasma sintering

Microstructures and mechanical properties of TiB2 composite ceramics with co-addition of Ti and TiC fabricated by SPS

Preparation of TiB2–SiC composites toughened with interlocking microstructure by self-assembled TiB2 plates

Densification behavior and mechanical properties of the spark plasma sintered monolithic TiB2 ceramics

Effect of Nano SiC on Microstructure and Mechanical Properties of BN-ZrO2-SiC Multiphase Ceramics

Fabrication, Microstructure, and Properties of SiC/Al 4 SiC 4 Multiphase Ceramics Via an In-Situ Formed Liquid Phase Sintering

Effect of B2O3 Addition on Low-temperature Sintering Behavior and Properties of SiC/h-BN Multiphase Ceramics

Structure and Properties of Spark Plasma Sintered SiC Ceramics with Oxide Additives

High‐strength TiB 2 ‐B 4 C Composite Ceramics Sintered by Spark Plasma Sintering

Fabrication, microstructure, and properties of SiC/Al4SiC4 multiphase ceramics via an in-situ formed liquid phase sintering

β→α Phase Transformation and Properties of Solid-State-Sintered SiC Ceramics with TaC Addition

Microstructure and Properties of TiB2-TiC-SiC Ternary Phase Ceramics Produced by High-Gravity Field Activated SHS of Ti-Si-B4C Powders

Microstructure and mechanical properties of spark plasma sintered SiC ceramics aided by B4C

Effects of theTiB2-SiC Volume Ratio and Spark Plasma Sintering Temperature on the Properties and Microstructure of TiB2-BN-SiC Composite Ceramics

Novel (ti, W)C–SiC–WSi2 Ceramics Fabricated Via in Situ Reaction Spark Plasma Sintering at 1600 °C

Effect of Additive Ti3SiC2 Content on the Mechanical Properties of B4C–TiB2 Composites Ceramics Sintered by Spark Plasma Sintering

Spark plasma sintering of B4C-TiB2-SiC composite ceramics using B4C, Ti3SiC2 and Si as starting materials

Low-temperature densification of TiB2 ceramic by the spark plasma sintering process with Ti as a sintering aid

Phase Formation, Microstructure and Mechanical Properties of TaB2-SiC Composites Synthesized by Reaction Hot Pressing: Effects of SiC Contents and Oxygen Impurity