Abstract:B4C/SiC (15 wt%) ceramic composite with 2 wt% carbon additive was fabricated via solid-phase pressureless sintering under an argon atmosphere for 60 min between 2100 degrees C and 2200 degrees C. The effects of the sintering temperature on the microstructure and mechanical properties of the B4C/SiC ceramic composites were studied in detail. The optimum values of the relative density, Vickers hardness, flexural strength, and fracture toughness of the B4C/SiC ceramic composite sintered at 2150 degrees C were 95.3%, 25.5 GPa, 296 MPa, and 2.81 MPa m(1/2), respectively. The microstructural investigations revealed that when the sintering temperature increases from 2100 degrees C to 2150 degrees C, sintered necks begin to grow and the densification zone increases. With sintering temperatures above 2150 degrees C, the grains grow rapidly such that the pores are not eliminated, causing the formation of large closed pores and resulting in a decrease in the relative density and mechanical properties of the B4C/SiC ceramic composite. The plate-like and irregular SiC grains are uniformly dispersed in the B4C matrix to inhibit B4C grain growth. The interface between SiC and B4C is clean and narrow, and the clean boundary suggests strong binding, which contributes to the mechanical properties of the B4C/SiC ceramic composite. At 2150 degrees C, the C additive undergoes significant crystallisation, forming lamellar structures with high aspect ratios, thereby promoting the pores in the ceramic composite to be discharged to the outside through volume diffusion to obtain a denser sintered body. The interface between B4C and graphite is a semi-coherent interface that increases the flexural strength with a low defect concentration. The main toughening mechanisms of the B4C/SiC ceramic composite are crack deflection and crack branching around the SiC grains and crack bridging by SiC grains in the wake of the crack tip. (C) 2019 Elsevier B.V. All rights reserved.

Spark plasma sintering of B4C-TiB2-SiC composite ceramics using B4C, Ti3SiC2 and Si as starting materials

High‐strength TiB 2 ‐B 4 C Composite Ceramics Sintered by Spark Plasma Sintering

B4C-TiB2 Composite Ceramics with Ultra-High Fracture Toughness Fabricated by Spark Plasma Sintering

Spark plasma sintering of B4C–ZrB2 and B4C–ZrB2–SiC ceramics

Microstructure and mechanical behaviour of transient liquid phase spark plasma sintered B4C–SiC–TiB2 composites from a B4C–TiSi2 system

Effect of Additive Ti3SiC2 Content on the Mechanical Properties of B4C–TiB2 Composites Ceramics Sintered by Spark Plasma Sintering

Enhancement mechanical properties of in-situ preparated B4C-based composites with small amount of (Ti3SiC2+Si)

Microstructure and Mechanical Properties of B4C Ceramics by Spark Plasma Sintering

Densification and Mechanical Properties of Spark Plasma Sintered B4C with Si as a Sintering Aid

Toughening mechanism of B4C/TiB2 ceramic materials by in situ reaction via spark plasma sintering

B4C‒TiB2 composite with modified microstructure and enhanced properties from optimal size coupling of raw powders

Processing and mechanical properties of B4C-SiCw ceramics densified by spark plasma sintering

Microstructure and Mechanical Properties of B4C Matrix Composites Sintered with (Tib2+al)

Microstructure and Mechanical Properties of B4C Densified by Spark Plasma Sintering with Si As a Sintering Aid

Enhanced Mechanical Properties of Nanocrystalline B4C–SiC Composites by In-Situ High Pressure Reactive Sintering

The Effect of CNTs on the Spark Plasma Sintering Densification Behavior and Mechanical Properties of B4C-Si Powders

Preparation of dense B4C ceramics by spark plasma sintering of high-purity nanoparticles

Transient Liquid Phase Spark Plasma Sintering of B4C-based Ceramics Using Ti-Al Intermetallics As Sintering Aid

In situ reaction synthesis of Ti–TiB composites containing high volume fraction of TiB by spark plasma sintering process

Effect of Sintering Temperature on the Mechanical Properties and Microstructures of Pressureless-Sintered B4C/SiC Ceramic Composite with Carbon Additive

B4C-based hard and tough ceramics densified via spark plasma sintering using a novel Mg2Si sintering aid