High-temperature Desulfurization of Carbide Slag and Bauxite During Coal Combustion

程军,周俊虎,刘建忠,周志军,曹欣玉,岑可法

DOI: https://doi.org/10.3321/j.issn:0253-2468.2003.05.015

2003-01-01

Abstract:The desulfurization property of carbide slag and bauxite is studied in coal combustion at high temperature. It is found that when carbide slag and bauxite are simultaneously added into Huangling coal, the first sulfur release rate peak derived from coal combustion at lower temperature is similar to that with carbide slag alone, while the second sulfur release rate peak obtained at higher temperature dramatically decreases. Therefore, the sulfur removal efficiency is distinctly promoted from 30.5% to 45.19% at 1200℃. It is shown by XRD and SEM analysis that the CaO composition in carbide slag and the Al 2O 3 composition in bauxite both react with the CaSO 4, which is derived from the sulfation reaction in coal combustion, to produce a new heat-resisting phase of 3CaO·3Al 2O 3·CaSO 4. This is the main reason why the sorbent composed of carbide slag and bauxite has better desulfurization property than the carbide slag alone. Another reason is that adding bauxite into carbide slag enhances the melt degree of the desulfurization residue, which provides more chances for melted silicate matter to envelop the sulfation product CaSO 4 and prevent it from thermal decomposition.