The Effect of Si on CO₂ Methanation over Ni-xSi/ZrO₂ Catalysts at Low Temperature

Li Li,Ye Wang,Qing Zhao,Changwei Hu

DOI: https://doi.org/10.3390/catal11010067

IF: 3.9

2021-01-01

Catalysts

Abstract:A series of Ni-xSi/ZrO2 (x = 0, 0.1, 0.5, 1 wt%, the controlled contents of Si) catalysts with a controlled nickel content of 10 wt% were prepared by the co-impregnation method with ZrO2 as support and Si as a promoter. The effect of different amounts of Si on the catalytic performance was investigated for CO2 methanation with the stoichiometric H-2/CO2 molar ratio (4/1). The catalysts were characterized by BET, XRF, H-2-TPR, H-2-TPD, H-2-chemisorption, CO2-TPD, XRD, TEM, XPS, and TG-DSC. It was found that adding the appropriate amount of Si could improve the catalytic performance of Ni/ZrO2 catalyst at a low reaction temperature (250 degrees C). Among all the catalysts studied, the Ni-0.1Si/ZrO2 catalyst showed the highest catalytic activity, with H-2 and CO2 conversion of 73.4% and 72.5%, respectively and the yield of CH4 was 72.2%. Meanwhile, the catalyst showed high stability and no deactivation within a 10 h test. Adding the appropriate amount of Si could enhance the interaction between Ni and ZrO2, and increase the Ni dispersion, the amounts of active sites including surface Ni-0, oxygen vacancies, and strong basic sites on the catalyst surface. These might be the reasons for the high activity and selectivity of the Ni-0.1Si/ZrO2 catalyst.