Abstract:For CO2 methanation reaction, a Mg species is often utilized as the alkaline promotor for Ni based catalysts to enhance the low-temperature catalytic activity. Herein, based on a pioneer ordered mesoporous NiO-Al2O3 catalyst, a Mg alkaline promotor had been incorporated into the ordered mesoporous framework via a one-pot evaporation induced self-assembly (EISA) strategy. As a result, the ordered mesoporous NiO-MgO-Al2O3 composite oxides with Mg/Al molar ratios in a wide range (0-10%) were successfully fabricated and directly utilized as the catalysts for CO2 methanation reaction. These mesoporous catalysts were carefully characterized by X-ray diffraction, N-2 adsorption-desorption, transmission electron microscopy, selected area electron diffraction, energy dispersive spectrometer, X-ray photoelectron spectroscopy, H-2 temperature-programmed reduction, and CO2 temperature-programmed desorption measurements. It was found that the ordered mesoporous materials with large specific surface areas (180.8-232.8 m(2) g(-1)), big pore volumes (0.37-0.43 cm(3) g(-1)), and narrow pore size distributions (around 9.5 nm) could be successfully retained after the calcination at 700 degrees C. The highly dispersed Ni species were strongly interacted with the mesoporous framework in the form of NiAl2O4 spinel. The incorporation of the Mg progressively increased the surface basicity of these catalysts, which could intensify the chemisorption and activation of CO2 during the CO2 methanation reaction. Therefore, the low-temperature catalytic activity was significantly enhanced. The "volcano-shape curve" relationship between the Mg/Al molar ratio and catalytic activity had been interestingly observed, suggesting only appropriate surface basicity could obtain the optimum catalytic activity. Besides, there was no evident deactivation over these mesoporous catalysts after 50 h long-term stability tests due to the confinement effect of the mesoporous framework. Therefore, the present ordered mesoporous NiO-MgO-Al2O3 materials could be considered as a series of potential catalyst candidates for CO2 methanation.

Zeolite-Supported Ni Catalysts for CO2 Methanation: Effect of Zeolite Structure and Si/Al Ratio

Impact of varied zeolite materials on nickel catalysts in CO 2 methanation

CO2 Methanation over the Ni-based Catalysts Supported on the Hollow ZSM-5 Zeolites: Effects of the Hollow Structure and Alkaline Treatment

Balance effect between Ni dispersion and hydrophobicity in CO 2 methanation over Ni/ZSM-5

Carbon Dioxide Reforming of Methane over Nickel-Supported Zeolites: A Screening Study

CO<sub>2</sub> methanation over Ni/ZSM-5 catalysts: The effects of support morphology and La<sub>2</sub>O<sub>3</sub> modification

Efficient and Stable Ni/ZSM-5@MCM-41 Catalyst for CO 2 Methanation

CO2 methanation over Ni/ZSM-5 catalysts: The effects of support morphology and La2O3 modification

Insights into the Zn Promoter for Improvement of Ni/SiO 2 Catalysts Prepared by the Ammonia Evaporation Method toward CO 2 Methanation

CO2 Methanation over CoNi Bimetal-Doped Ordered Mesoporous Al2O3 Catalysts with Enhanced Low-Temperature Activities

Highly Dispersed Ni-La Catalysts over Mesoporous Nanosponge MFI Zeolite for Low-Temperature CO2 Methanation: Synergistic Effect Between Mesoporous and Microporous Channels

Synthesis of nickel catalysts supported on Zr-doped ordered mesoporous Al2O3 and their catalytic performance for low-temperature CO2 reforming of CH4

Cobalt-doped Ni-based catalysts for low-temperature CO 2 methanation

Study on CO2 reforming of methane to syngas over Al 2O3-ZrO2 supported Ni catalysts prepared via a direct sol-gel process

NiAlFe catalysts based on hydrotalcite-like precursors for low temperature CO 2 methanation: Electronic effects among components and intrinsic activity of Ni site

The Effect of Si on CO2 Methanation over Ni-xSi/ZrO2 Catalysts at Low Temperature

Aqueous Miscible Organic LDH Derived Ni-Based Catalysts for Efficient CO2 Methanation

Alkaline-promoted Ni based ordered mesoporous catalysts with enhanced low-temperature catalytic activity toward CO2 methanation

Optimizing CO2 methanation: effect of surface basicity and active phase reducibility on Ni-based catalysts

Meso-porous Ni/Mg/Al catalysts for methane reforming with CO2

CO2 Methanation over Nickel-Based Catalysts Supported on MCM-41 with in Situ Doping of Zirconium