A flame retardant fabric nanocoating based on nanocarbon black particles@polymer composite and its fire-alarm application
Long Xia,Yan Lv,Zhongxi Miao,Lili Luo,Weiang Luo,Yiting Xu,Conghui Yuan,Birong Zeng,Lizong Dai,Long Xia,Yan Lv,Zhongxi Miao,Lili Luo,Weiang Luo,Yiting Xu,Conghui Yuan,Birong Zeng,Lizong Dai
DOI: https://doi.org/10.1016/j.cej.2021.133501
IF: 15.1
2022-04-01
Chemical Engineering Journal
Abstract:Facile fabrication of fire-warning sensors with low-cost and high-strength has always been a considerable challenge for materials scientists. Herein, Carbon black (CB) nanoparticles with core-shell structure (denoted as CB@KF) were prepared by in-situ polymerization. And a novel fire-warning sensor (denoted as CB@KF-CF) with temperature sensing, fire-warning, flexibility and high strength was fabricated by coating a flame retardant coating, which consists of PVA, CB@KF, and Carbon nanotubes (CNT) on cotton fabric. Benefiting from the flame retardancy and carbonization performance of CB@KF, CB@KF-CF possessed much better flame retardancy and fire-warning properties. Especially, CB@KF-CF exhibited a shorter alarm time to abnormal high temperature (350 °C) and fire, which can warn at 8 s and 4 s respectively. Meanwhile, the char length of CB@KF-CF was 7.8 cm after the Vertical flame test (VFT) and the Total heat release rate (THR) of CB@KF-CF was also reduced by more than 50%. Ultimately, the formation mechanism of the dense char layer and the conductive paths were also illustrated. These results show that the preparation of fire-warning sensor described in this paper has broad application prospects.
engineering, chemical, environmental