Facile Construction of a Flexible Film with Ultrahigh Thermal Conductivity and Excellent Flame Retardancy for a Smart Fire Alarm
Zhencai Qu,Kun Wu,Chang-an Xu,Yue Li,Enxiang Jiao,Bing Chen,Huifa Meng,Xiaohua Cui,Kunxin Wang,Jun Shi,Zhencai Qu,Kun Wu,Chang-an Xu,Yue Li,Enxiang Jiao,Bing Chen,Huifa Meng,Xiaohua Cui,Kunxin Wang,Jun Shi
DOI: https://doi.org/10.1021/acs.chemmater.1c00113
IF: 10.508
2021-04-26
Chemistry of Materials
Abstract:Design and development of intelligent fire warning materials with rapid response capabilities has always been an urgent need for the safety of many flammable materials in their applications. Herein, an aminated black phosphorene (BP-NH<sub>2</sub>) prepared by ball milling was employed to connect with graphene oxide (GO) via covalent bonds to fabricate a flexible film with ultrahigh thermal conductivity and remarkable flame retardancy. The thermal diffusivity of the RPNG 20 film is as high as 1496.87 ± 51.11 mm<sup>2</sup> s<sup>–1</sup>, and its thermal conductivity is also up to 1085.74 ± 37.08 W m<sup>–1</sup> K<sup>–1</sup>, which is in full agreement with the theoretical calculation value (1086.9 ± 59.1 W m<sup>–1</sup> K<sup>–1</sup>) of the multilayer graphene nanosheets reported in the previous literature. The effective medium theoretical calculations show that the interface thermal resistance has been reduced to 1/367 of that of pure graphene, which promotes the heat transfer of phonons. Simultaneously, it displays excellent flame-retardant properties. The peak of the heat release rate (PHRR) value is only 12.46 W g<sup>–1</sup>, resulting in a 96.57% decrease compared with that of the pure GO film (363.17 W g<sup>–1</sup>), which is attributed to the formation of an intumescent flame-retardant system. More importantly, when encountering a flame attack, the unreduced flexible film demonstrates an extremely fast fire alarm response capability of less than 1 s and can continue to work after leaving the fire, which is ascribed to the high degree of carbonization after contacting with fire. This covalent linkage strategy provides a new thought for the preparation of multifunctional films to improve the fire prevention and protection response capabilities in the smart fire alarm device.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.chemmater.1c00113?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.chemmater.1c00113</a>.Fire alarm device connected with the RGO film when it is connected to the switch (<a class="ext-link" href="/doi/suppl/10.1021/acs.chemmater.1c00113/suppl_file/cm1c00113_si_001.mp4">MP4</a>)Fire alarm device connected with the GO film when encountering a flame attack (<a class="ext-link" href="/doi/suppl/10.1021/acs.chemmater.1c00113/suppl_file/cm1c00113_si_002.mp4">MP4</a>)Fire alarm device connected with the PNG 20 film when encountering a flame attack (<a class="ext-link" href="/doi/suppl/10.1021/acs.chemmater.1c00113/suppl_file/cm1c00113_si_003.mp4">MP4</a>)Figures S1–S3 providing additional analysis results for the BP and BP-NH<sub>2</sub> including the XRD patterns, Raman spectra, XPS spectra, FTIR spectra, TG analysis, SEM images, AFM images, and TEM images.; Figure S4–S5 offering the digital image of the GO film with different addition amounts of BP-NH<sub>2</sub> and the flexibility, toughness of tensile testing, and the tensile stress–strain curves; Figure S6 supplying the SEM image of the cross section of the GO film, RGO film, and RPNG 20 film; Figure S7 providing the characterization of the GO film and RPNG 20 film including the XRD, Raman, XPS, FTIR, fluorescence, and solid NMR spectra; Figure S8 offering the TGA curves and HRR curves for the GO, RGO, RPNG 20, and RPG 20 films; Figures S9–S11 supplying the characterization of residues after combustion; Figure S12 offering the electrical resistance value and electrical current of PNG 20 before and after ignition; and Table S1 providing the densities (ρ), thermal diffusivities (α), specific heat capacities (<i>C</i><sub>p</sub>), and corresponding thermal conductivities (<i>K</i>) of the samples (<a class="ext-link" href="/doi/suppl/10.1021/acs.chemmater.1c00113/suppl_file/cm1c00113_si_004.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical