Nano polycrystalline structured ZnSe synthesized by the hydrothermal elemental-direct-reaction method: Structures, Raman and photoluminescence properties
Peng Fei Ji,Yong Li,Peng Fei Li,Ya Juan Hao,Yue Li Song,Feng Qun Zhou
DOI: https://doi.org/10.1016/j.jlumin.2022.119087
IF: 3.6
2022-10-01
Journal of Luminescence
Abstract:Nano polycrystalline ZnSe (np-ZnSe) have been synthesized by a hydrothermal elemental direct reaction of metal Zn with Se in ethylenediamine at 180 °C for 6 h, which shows an irregular structure and is characterized with nanobelts and nanowires. A broad Raman spectrum with a strong TO phonon peak has been observed, which can be decomposed into six peaks located at ∼143 cm−1, ∼175 cm−1, ∼207 cm−1, ∼233 cm−1, ∼253 cm−1 and ∼275 cm−1, respectively, are assigned to 2 TA mode, the interaction of two-phonon with disorder, TO mode, the scattering from the simple substance Se, LO mode and the interface of ZnSe–ZnO. The A band, B band and C band from photoluminescence (PL) at 300 K are attributed to bandgap, transition from Zn interstitials to the valence band and the nano polycrystalline structure, respectively. Compared with PL at 16 K, the emissions from bandgap show blueshift with the decreasing temperature. Redshift of B bands and C bands is due to the carrier scattering with LO phonon of np-ZnSe. From PL at 16 K, the emission of ∼701 nm is attributed to the recombination from oxygen-related states. It is believed that understanding of the structures, Raman and PL properties are beneficial to the application of np-ZnSe in the optoelectronic field.
optics