Abstract:In this work, two isothermal sections of the Co-Ta-Si ternary system at 900 °C and 1100 °C are constructed in the whole composition range via phase equilibrium determination with the help of electron probe microanalysis (EPMA) and X-ray diffraction (XRD) techniques. Firstly, several reported ternary phases G (Co16Ta6Si7), G″ (Co4TaSi3), E (CoTaSi), L (Co3Ta2Si) and V (Co4Ta4Si7) are all re-confirmed again. The G″ phase is found to be a kind of high-temperature compound, which is unstable at less than 1100 °C. Additionally, the L phase with a large composition range (Co32-62Ta26-36Si10-30) crystallizes with a hexagonal crystal structure (space group: P63/mmc, C14), which is the same as that of the binary high-temperature λ1-Co2Ta phase. It can be reasonably speculated that the ternary L phase results from the stabilization toward low-temperature of the binary λ1-Co2Ta through adding Si. Secondly, the binary CoTa2 and SiTa2 phases are found to form a continuous solid solution phase (Co, Si)Ta2 with a body-centered tetragonal structure. Thirdly, the elemental Si shows a large solid solubility for Co-Ta binary compounds while the Ta and Co are hardly dissolved in Co-Si and Ta-Si binary phases, respectively.

Experimental Investigations of Phase Equilibria in the Ta-V-Cr Ternary System

Experimental Investigation of Phase Equilibria in the Ti-Cr-V System at 1000–1200 °C

Experimental Investigation and Thermodynamic Assessment of Phase Equilibria in the Al-Ta-V Ternary System

Experimental Investigation of Phase Equilibria in the Fe-Nb-Ta System

Experimental Investigation of Phase Equilibria in the Co-Ta-Si Ternary System

Phase equilibria in Ni–Ti–Ta ternary system

Experimental determination of the liquidus projection of the B-Cr-Ti system

Experimental Investigation of Phase Equilibria in the Nb-Si-V Ternary System

Phase relationship of the Ag–Zr–Cr system at 1000 and 750°C

Experimental isothermal section of the system Cr-Nb-Ru at 1100 °C

Phase Relationship Of The Ag-Z-Cr System At 1000 And 750 Degrees C

Experimental determination of isothermal sections for the Co-rich corner of the Co-Cr-Ti system at 800 and 900 °C

Experimental study of the phase relations in the Fe–Cr–Si ternary system at 700°C

Phase equilibria in Co−Al−Re ternary system at 1100 and 1300 °C

Experimental Investigation and Thermodynamic Description of the Fe–Ta–Ti System

Phase equilibria in Co-Ti-Re ternary system

Experimental investigation on the 800 degrees C isothermal section of the Ti-Ni-Nb ternary system

Study on the phase equilibria of the Ti–Ni–Nb ternary system at 900°C

Third-Generation Thermodynamic Descriptions for Ta-Cr and Ta-V Binary Systems

Phase Equilibria of the Ternary Ni-Cr-Zr System and Interfacial Reactions in the Ni-Cr/Zr Couples

Study on the phase equilibria of the Ti-Ni-Nb ternary system at 900 degrees C