Experimental Investigation and Thermodynamic Assessment of Phase Equilibria in the Al-Ta-V Ternary System
Cuiping Wang,Debin Zheng,Zhangcan Zheng,Lianzhang Wu,Jianping Le,Yihui Guo,Yixiong Huang,Jinbin Zhang,Yong Lu,Xingjun Liu
DOI: https://doi.org/10.1007/s11669-024-01102-1
2024-04-08
Journal of Phase Equilibria and Diffusion
Abstract:The phase equilibria in the Al-Ta-V ternary system at 1000 °C and 1200 °C have been studied by using electron probe microanalysis and x-ray diffraction. τ-Al 2.9 Ta 2.7 V 1.4 phase was found in the Al-Ta-V ternary system in both isothermal sections. The addition of V stabilizes the Al 69 Ta 39 phase at 1000 °C. The line compound Al 3 (V,Ta) (D0 22 -type) forms a continuous phase region from the Al-V side to the Al-Ta side at the two temperatures. Based on our experimental results, reported liquidus projection of the ternary Al-Ta-V system and thermodynamic data of the binary systems of Al-V, Al-Ta and V-Ta, a thermodynamic evaluation of Al-Ta-V system was carried out by CALPHAD method. A set of reliable thermodynamic parameters for the Al-Ta-V system was obtained. The current calculation results agree well with the available experimental data. The invariant reaction scheme of Al-Ta-V ternary system was presented. The present study could provide essential experimental and thermodynamic data for establishing a comprehensive Co-based superalloy database.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering