Abstract:The phase equilibria in the Zr–ZrCo–ZrNi system at subsolidus temperature and at 900 and 800°C were first studied using physicochemical analysis methods, and solidus surfaces and isothermal sections at 900 and 800°C were constructed. Isomorphic Zr2Co and Zr2Ni compounds with a tetragonal crystal structure of AlCu2 (θ) type form a continuous series of solid solutions dividing the Zr–ZrCo–ZrNi system into two subsystems: Zr–Zr2Co–Zr2Ni and ZrCo–ZrNi–Zr2Ni–Zr2Co. The equilibria on the solidus surface of the Zr–Zr2Co–ZrCo–Zr2Ni system and at 900°C differ significantly. This is associated with the Zr3Co-based η phase formed by peritectoid reaction 〈β − Zr〉 + 〈Zr2Co〉 → η at 980°C, being close to theL ↔ θ + β eutectic crystallization temperature (986°C), in the binary Zr–Co system. At 900 and 800°C, the 𝜂 phase dissolves up to 14.5% Ni. The solidus surface of the ternary Zr2Co–Zr2Ni–ZrCo–ZrNi system shows a three-phase equilibrium of the θ phase with the ZrCo (δ) and ZrNi (δ2) phases of the ZrCo–ZrNi quasibinary section: δ + δ2 + θ. The plane of this tie-line triangle extends significantly at 900 and 800°C as the solubility of nickel in the cubic ZrCo-based phase of CsCl type changes. At room temperature, all alloys of the ZrCo–ZrNi–Zr2Ni–Zr2Co subsystem should contain three phases: δ + δ2 + θ. The solidus surface of the Zr–ZrCo ZrNi system is thus completed by surfaces corresponding to the homogeneity regions of the δ, δ2, δ, and β phases, θ + δ + δ2 tie-line triangle plane, and ruled surfaces representing the upper boundary of the two-phase θ + δ2, θ + δ, and θ + δ volumes. At 900 and 800°C, two three-phase equilibria, η + θ + β and δ + δ2 + θ, are observed in the system.

Phase Relationship Of The Ag-Z-Cr System At 1000 And 750 Degrees C

Phase relationship of the Ag–Zr–Cr system at 1000 and 750°C

Phase equilibria thermodynamics and solidified microstructure in the Ag-Cr-Zr system

Ab Initio Calculations of the Thermodynamics and Phase Diagram of Zirconium

Phase Equilibria of the Ternary Ni-Cr-Zr System and Interfacial Reactions in the Ni-Cr/Zr Couples

Experimental determination and thermodynamic calculation of phase equilibria in Ag-Zr-Y system

Solidification paths and phase equilibria at 873 and 673 K in the Al-Er-Zr system

Experimental Investigation of Phase Equilibria in the Ti-Cr-V System at 1000–1200 °C

Measurement of the phase equilibria in the Al–Zr–Y system at 673 and 823 K

Phase Relationships in the Al-rich Region of the Al-Y-Zr System

Experimental study of the phase relations in the Fe–Cr–Si ternary system at 700°C

Phase Equilibria In The Fe-Nb-Zr Ternary System At 1,200 A Degrees C

Thermodynamic description of the Al–Ag–Zr system and discovery of the high-strength ternary phase Al1.84Ag0.16Zr

Phase diagrams of the Ag-In-Zn ternary system

Experimental isothermal section of the system Cr-Nb-Ru at 1100 °C

Liquidus Projection and Isothermal Section of the Ag-In-Zn Ternary System

Experimental Study on Phase Relationships in the Co-rich Portion of the Co–Ti–Zr System

Phase equilibria in Co−Al−Re ternary system at 1100 and 1300 °C

Phase equilibria in the Fe–Nb–Zr ternary system at 1,200 °C

The Co–Ni–Zr Phase Diagram in the Zr–ZrCo–ZrNi Region I. Phase Equilibria in the Zr–ZrCo–ZrNi System at Subsolidus Temperature, 900°C, and 800°C

Phase Equilibria of the Ag-Al-Au Ternary System and Interfacial Reactions in the Au-xAg/Al Couples at 450 °C