Study on the Effect of the Pre-treatment Temperature on Li1.2Mn0.54Ni0.13Co0.13O2 Cathode Material

Yi Jin,Chen Hu,Cheng,Dandan Sung,Chunyu Du,Jiyuan Jian,Geping Yin

DOI: https://doi.org/10.20964/2020.11.27

IF: 1.541

2020-01-01

International Journal of Electrochemical Science

Abstract:Lithium-rich manganese-based cathode materials (LMO) have been considered the most promising candidate materials for next-generation lithium-ion batteries due to their high theoretical specific capacity (>300 mAh g(-1)). However, the low initial Coulombic efficiency, significant capacity fading and poor rate capability have restricted their commercial application. In particular, the synthesis process of lithium-rich materials plays a decisive role in their structure and electrochemical performance. This paper mainly studies the effect of the pre-treatment temperature on the structure and performance of lithium-rich materials. The calcination temperature affects the performance of the lithium-rich material by changing the structure of the metal oxide (MO). Consequently, 600 degrees C-LMO has better cycling stability and rate performance than 700 degrees C-LMO and 500 degrees C-LMO. 600 degrees C-LMO delivers a high initial charge capacity of 252 mAh g(-1) with a large initial Coulombic efficiency of 81.4% at 0.1 C. After cycling 50 times, large and stable discharge capacities of 229 mAh g(-1) can be obtained. Both XRD and SAED characterize the presence of a spinel structure in 600 degrees C-LMO, and the heterogeneous lithium-rich material shows excellent cycling stability and rate performance.