Abstract:The existing research about ductile grinding of fused silica glass was mainly focused on how to carry out ductile regime material removal for generating very "smoothed" surface and investigate the machining-induced damage in the grinding in order to reduce or eliminate the subsurface damage.The brittle/ductile transition behavior of optical glass materials and the wear of diamond wheel are the most important factors for ductile grinding of optical glass.In this paper,the critical brittle/ductile depth,the influence factors on brittle/ductile transition behavior,the wear of diamond grits in diamond grinding of ultra pure fused silica（UPFS） are investigated by means of micro/nano indentation technique,as well as single grit diamond grinding on an ultra-stiff machine tool,Tetraform "C".The single grit grinding processes are in-process monitored using acoustic emission（AE） and force dynamometer simultaneously.The wear of diamond grits,morphology and subsurface integrity of the machined groves are examined with atomic force microscope（AFM） and scanning electron microscope（SEM）.The critical brittle/ductile depth of more than 0.5 μm is achieved.When compared to the using roof-like grits,by using pyramidal diamonds leads to higher critical depths of scratch with identical grinding parameters.However,the influence of grit shapes on the critical depth is not significant as supposed.The grinding force increased linearly with depth of cut in the ductile removal regime,but in brittle removal regime,there are large fluctuations instead of forces increase.The SEM photographs of the cross-section profile show that the median cracks dominate the crack patterns beneath the single grooves.Furthermore,The SEM photographs show multi worn patterns of diamond grits,indicating an inhomogeneous wear mechanism of diamond grits in grinding of fused silica with diamond grinding wheels.The proposed research provides the basal technical theory for improving the ultra-precision grinding of UPFS.

Sliding of a Diamond Sphere on Fused Silica under Ramping Load

An Investigation into the Densification-Affected Deformation and Fracture in Fused Silica under Contact Sliding

An analytical method for assessing the initiation and interaction of cracks in fused silica subjected to contact sliding

Critical condition of subsurface crack formation for optics

Propagation Regularity of Sub-Surface Crack in Static Indentation of Fused Silica by Single Abrasive

Scratch test of soda-lime glass

Models of grinding-induced surface and subsurface damages in fused silica considering strain rate and micro shape/geometry of abrasive

Coupled SPH-FEM modeling of Berkovich indenter scratching of single-crystal silicon

A material point method based investigation on crack classification and transformation induced by grit geometry during scratching silicon carbide

Surface damage resistance and yielding of chemically strengthened silicate glasses: From normal indentation to scratch loading

Surface Damage Mechanism of Monocrystalline Si under Mechanical Loading

Micro/Nano Indentation and Single Grit Diamond Grinding Mechanism on Ultra Pure Fused Silica

Densification Effects on the Fracture in Fused Silica under Vickers Indentation

Evaluation of Subsurface Crack Depth During Scratch Test for Optical Glass Bk7

Theoretical modeling and experimental analysis of single-grain scratching mechanism of fused quartz glass

Strain-rate Dependence of Surface/subsurface Deformation Mechanisms During Nanoscratching Tests of GGG Single Crystal

Nanoindentation and Nanoscratch Tests of YAG Single Crystals: an Investigation into Mechanical Properties, Surface Formation Characteristic, and Theoretical Model of Edge-Breaking Size

Hardness and Friction Coefficient of Fused Silica under Scratching Considering Elastic Recovery

Numerical and experimental investigation on ductile deformation and subsurface defects of monocrystalline silicon during nano-scratching

&Lt;title>deformation of Fused Silica: Nanoindentation and Densification</title>

A Quantitative Analysis of the Indentation Fracture of Fused Silica