Abstract:The paper investigated the annealing temperature dependence of electrical and structural properties for Ni (50 nm)/Ti (60 nm)/W (60 nm) Ohmic contacts simultaneously formed on n- and p-type 4H-SiC by in-depth electrical and physical characterization. With the annealing temperature rising in the range of 900 °C–1050 °C, the specific contact resistances (SCRs) of both n- and p-type Ohmic contacts monotonously decreased with a similar trend in the range of 1 × 10−4–1 × 10−6 Ω cm2, which was favorable for the simultaneous formation of n- and p-type Ohmic contacts with lower SCRs in the active region. For n-type Ohmic contacts, the variation of SCRs with annealing temperatures was correlated to the relative proportion of the total contact area occupied by the (220) plane compared to the other planes for the polycrystalline and textured δ-Ni2Si film at the contact interface characterized by x-ray diffraction. Furthermore, the surface morphology of Ohmic contacts under different annealing temperatures was highly similar with almost identical root mean square roughness of about 6.2 nm measured by atomic force microscopy (AFM), which was thought to be smooth enough for the wire bonding process from the perspective of device applications. The distinct W layer with no evidence of obvious intermixing and the great distance of released free carbon away from the contact surface makes the surface morphology smooth and uniform.

Annealing Temperature on Contact Properties Between Nickel Film and Hydrogen-Terminated Single Crystal Diamond

Reliable Ohmic Contact Properties for Ni/Hydrogen-Terminated Diamond at Annealing Temperature up to 900 °C

Thermal stability investigation for Ohmic contact properties of Pt, Au, and Pd electrodes on the same hydrogen-terminated diamond

Palladium Ohmic Contact on Hydrogen-Terminated Single Crystal Diamond Film

Ohmic Contact of Pt/Au on Hydrogen-Terminated Single Crystal Diamond

Effect of Annealing Temperature on Ti/Al/Ni/Au Ohmic Contacts on Undoped AlN Films

Effects of Rapid Thermal Annealing on the Contact of Tungsten/p-Diamond

Thermal Annealing Effects on Ni/Au Contacts to P Type Gan in Different Ambient

Thermal annealing induced graphite/diamond structure processed by high-voltage hydroxide ion treatments

Modification of an Electroplated Nickel Interlayer Surface by Annealing Heat Treatment for Diamond Deposition on Tungsten Carbide

Ohmic Contact Between Iridium Film And Hydrogen-Terminated Single Crystal Diamond

Interaction and ohmic contact between NiCr alloy and a-Si:H thin films at low temperatures

Annealing Temperature Dependent Properties for Ni/Ti/W Ohmic Contacts Simultaneously Formed on N- and P-Type 4H-Sic

Effects of Ag on Electrical Properties of Ag/Ni/P-Gan Ohmic Contact

Influence Of Annealing Temperature On Film Morphology And Tribological Performance Of Tisin-Ag Coating

Microstructure Evolution of Oxidized Ni/Au Ohmic Contacts to P-Gan Studied by X-Ray Diffraction

Ohmic Contact Formation of Ti/Al/Ni/Au to N-Gan by Two-Step Annealing Method

Performance Comparison of Pt/Au and Ni/Au Schottky Contacts on Alxga1-X N/Gan Heterostructures at High Temperatures

Temperature Dependence of the Specific Resistance in Ti/Al/Ni/Au Ohmic Contacts on (nh4)2sx Treated N-Type GaN

Growth and Annealing Study of Hydrogen-Doped Single Diamond Crystals under High Pressure and High Temperature

Study of Ti/Au, Ti/Al/Au, and Ti/Al/Ni/Au ohmic contacts to n -GaN