Abstract:The near stoichiometric SiC fiber has been reported to play significant roles in the application of aero‐engine field. An in‐depth understanding on the degradation mechanism of the fiber during its corrosion in air and under a simulated aeroengine environment (PH2O: PO2: PAr = 14:8:78 kPa) will shine a light on the performance evaluations of the near stoichiometric SiC fiber‐based materials as well as the development of their potential applications. In this study, .XRD, SEM, and FIB‐TEM were utilized to analyze the mechanical properties and microstructure of the fiber. After oxidation in dry air and Ar‐H2O‐O2 for 1h, respectively the fiber strength retention rate has been found to decreases with the increased oxidation temperature. The raise in oxidation temperature also led to the increasing of the thickness and the crystallization rate of the oxide scale. The most different oxidation behavior of SiC being treated under the simulated environment than in air is the lower oxidation activation energy and the higher crystallization activation energy for cristobalite. Water vapor can promote the oxidation reaction and inhibit the crystallization of cristobalite in the oxide scale. Few significant differences have been observed otherwise in the oxidation process and oxidation chromatography crystallization mechanism of fibers being treated under different conditions.. The increase of oxide layer thickness and the formation of cristobalite impair the structural integrity and compactness of the oxide scale and thus leads to the deterioration of the mechanical properties of SiC fibers. Therefore, it is proposed that oxidation resistance of SiC fiber can be improved by insulating the reaction between the oxidizing agents and the SiC fiber, or by increasing the crystallization temperature of cristobalite in the oxidation process and reducing the crystallization rate. This article is protected by copyright. All rights reserved

Scheelite Coatings on SiC Fiber: Effect of Coating Temperature and Atmosphere

Strength Retention in Scheelite Coated SiC Fibers: Effect of the Gas Composition and Pre-Heat Treatment

Influence of SiC Coating Thickness on Mechanical Properties of SiCf/SiC Composite

Influence Of Sic Coating On The Oxidation Behavior Of Pan Carbon Fiber At Elevated Temperatures

Effects of the Ar flow rate on the composition, structure, and properties of near-stoichiometric SiC fibres that were annealed at 1600°C

Mechanical properties and microstructural evolution of Cansas-III SiC fibers after thermal exposure in different atmospheres

Degradation mechanism of near stoichiometric SiC fibers after air and Ar‐H2O‐O2 corrosion at 1000∼1500°C

Effect of long-time annealing at high temperature on the microstructure and mechanical properties of different types of SiC fibers

Oxidation and mechanical properties of SiC fibers after high temperature exposure in air and steam

Influence of SiC Nanowires on the Properties of SiC Coating for C/C Composites Between Room Temperature and 1500°C

Influence of SiC Coating on Antioxidation Property of Carbon Fibers

Effects of PyC coating on SiC fibers after ultra-high temperature annealing

High Temperature Oxidation Behavior of SiC Coating Materials

The fiber structure evolution and performance changes of SiC–ZrC fibers after 1600 °C heat treatment

Effect of heat treatment on the microstructure and properties of CVD SiC fiber

Strength degradation of SiC fibers with a porous ZrB2-SiC coating: Role of the coating porous structure

Long-time oxidation behavior of the nearly stoichiometric polycrystalline SiC fibers under air atmosphere at different temperatures

The Effect of Heat Treatment on the Properties of SiCf/SiC Composites Prepared with Different SiC Fibers

Structural evolution and mechanical properties of Cansas-III SiC fibers after thermal treatment up to 1700 °C

SiC Performance of Coated Fuel Particles under High-Temperature Atmosphere of Air

Improvement of Strength and Oxidation Resistance for SiC/graphite Composites by SiC Coating