Abstract:The residual stress is considered to be the driving force for the failure of ceramic/metal brazing joint. In this paper, the residual stress in a SiC/Nb joint is alleviated by using AgCuTi + B4C composite brazing filler. SEM, EDS and XRD are applied to characterised the microstructure of the joint, which is determined to be SiC/Ti3SiC2/Ag (s,s)+ Cu(s,s)+ TiB + TiC/TiCu + Nb(s,s)/Nb. The effects of the B4C strengthening phase mass fraction and the brazing temperature on the microstructure and the mechanical properties of the joint are investigated. It is found that the reaction products between B4C and the brazing filler (TiB whisker and TiC particles) uniformly distribute inside the joint if the mass fraction of the B4C is not higher than 1.5 wt% and when the amount of B4C reaches 2 wt%, the reaction products begin to agglomerate. With the rising of the brazing temperature, the thickness of the Ti3SiC2 reaction layer next to the ceramic increases and when the brazing temperature reaches 910 degrees C, another reaction layer of Ti5Si3 can be found adjacent to the Ti3SiC2 reaction layer. The strength of the joint first increases and then decreases with the increase of both the strengthening phase and the brazing temperature. The highest shear strength of the joint reaches 98 MPa when the joint is achieved at 890 degrees C using AgCuTi +1.5 wt%B4C brazing filler.

Brazing of SiC Ceramics Pretreated by Chromium Coating Using Inactive AgCu Filler Metal

Titanium-deposition Assisted Brazing of SiC Ceramics Using Inactive AgCu Filler

Effect of Brazing Parameters on the Microstructure and Properties of SiC Ceramic Joint with Zr-Cu Filler Metal

Interfacial Microstructure and Mechanical Properties of SiC Joints Achieved by Reactive Air Brazing Using Ag-V2O5 Filler

Brazing SiC Ceramic Using Novel B4C Reinforced Ag–Cu–Ti Composite Filler

Wetting Behavior and Brazing of Titanium‐coated SiC Ceramics Using Sn0.3Ag0.7Cu Filler

Microstructure and Shear Strength of SiC Joint Brazed with LiAlSiO4 Reinforced AgCuTi Composite Filler

Brazing SiC Ceramic to Al0.3CoCrFeNi High‐entropy Alloy Using Ag–Cu Filler Metal

Microstructural and mechanical properties of porous Si3N4 carbon coated ceramic brazed with a cobalt-silicon filler

Brazing of SiC ceramic to Al<sub>0.3</sub>CoCrFeNi high entropy alloy by graphene nanoplates reinforced AgCuTi composite fillers

Microstructure and Mechanical Properties of the SiC/Nb Joint Brazed Using AgCuTi + B4C Composite Filler Metal

Interfacial microstructure and mechanical property of ZrC-SiC ceramic and TiAl joint brazed with AgZr active filler metal

Brazing SiC Ceramics and Zr with CoCrFeNiCuSn High Entropy Alloy

Brazing of Ti-coated SiC Using a CoFeCrNiCu High Entropy Alloy Filler Via Electric Field-Assisted Sintering

Interface microstructure and mechanism of SiC ceramic vacuum brazed joint

Joining of SiC using CoFeCrNiCuTi high entropy alloy filler by electric current field assisted sintering

Brazing of ZrB2–SiC–C and GH99 with AgCuTi/SiC Interpenetrating Network Structural Composite As an Interlayer

Reaction mechanism and mechanical properties of SiC joint brazed by in-situ formation of Ti3SiC2

A novel high entropy CoFeCrNiCu alloy filler to braze SiC ceramics

Microstructure and Mechanical Property of Vacuum Brazed SiC Ceramic Joint

Microstructure and shear strength of SiC/Zr joint brazed with LiAlSiO4/graphene-coated Cu-foam composite interlayer