Abstract:Reducing the residual stresses and improving the mechanical strength of large-scale ceramic/metal brazing joints is an important problem that must be solved for its practical engineering application. Using composite filler with solid-state phase transformation ceramic particulates, it is theoretically feasible to relieve the residual stress and improve the mechanical properties of ceramic/metal brazed joints. In this study, Cu mesh, Ag-28Cu-2Ti (wt.%), and YSZ (0.6 mol.% Yttria-stabilized Zirconia solid-state phase transformation ceramic particulates) composite power fillers were used in the brazing of Ti3SiC2 ceramic and pure copper. The microstructure of joints and YSZ particulates in the interface was investigated and confirmed by SEM, EDS, STEM and TEM. In addition, the effect of YSZ particulates content on the mechanical properties of joints was investigated and evaluated by the shear strength. The results show that the interfacial phases were mainly Ti5Si3, TiC, TixCu, Ag (s, s), Cu (s, s) and YSZ particulates. Moreover, most of YSZ particulates undergo the solid-state phase transformation from t-ZrO2 to m-ZrO2 during the cooling process of brazing. The abnormal volume expansion of the solid-state phase transformation reduced the thermal mismatch between Ti3SiC2 ceramic and filler, thereby reducing the residual stress in the interface of joint. When using composite filler with 6wt.% YSZ particulates, the shear strength of Ti3SiC2/Cu joint reached the maximum. The maximum average shear strength of the joints was 80.2 MPa, which was about 103.6% more than the joint without YSZ particulates.This article is protected by copyright. All rights reserved

Wetting Behavior and Brazing of Titanium‐coated SiC Ceramics Using Sn0.3Ag0.7Cu Filler

Microstructure and properties of different carbon fiber reinforced ceramic composites brazed joint by Si-Ti alloy filler

Reaction mechanism and mechanical properties of SiC joint brazed by in-situ formation of Ti3SiC2

Solid-Liquid State Bonding of Si3N4 Ceramics with Ceramic-Modified Brazing Alloy

Microstructure and Shear Strength of SiC Joint Brazed with LiAlSiO4 Reinforced AgCuTi Composite Filler

Interfacial Structure and Formation Mechanism of Ultrasonic-Assisted Brazed Joint of Sic Ceramics with Al-12si Filler Metals in Air

Joining of SiC using CoFeCrNiCuTi high entropy alloy filler by electric current field assisted sintering

Joining of Ti-coated monolithic SiC using a SiCw/Ti3SiC2 filler by electric field-assisted sintering

Sonocapillary and wetting mechanism during ultrasonic brazing porous Si3N4 ceramics in air

SiC fiber strengthened Si 14Ti high-temperature filler alloy for brazing SiC f /SiC and C/C composites

Wetting and brazing of Cf/C composites with Si–Zr eutectic alloys: The formation of nano- and coarse-SiC reaction layers

Titanium metallization of Si3N4 ceramics by molten salt reaction: coating microstructure and brazing property

Improvement for Ti 3 SiC 2 /Cu joint brazed using composite fillers with abnormal expansion ceramic particulates

C/SiC composite-Ti6Al4V joints brazed with negative thermal expansion ZrP2WO12 nanoparticle reinforced AgCu alloy

Microstructure and mechanical properties of Si3N4 ceramic and (TiB + Y2O3)/Ti matrix composite joints brazed with AgCu/Cu foam/AgCu multilayered filler

Effect of Ti content on microstructure and mechanical properties of SiCf/SiC composites/GH536 superalloy joints brazed with CoFeCrNiCuTi high entropy filler

Effect of Brazing Parameters on the Microstructure and Properties of SiC Ceramic Joint with Zr-Cu Filler Metal

Flash brazing of SiC using Ag-Cu-Ti alloy at ultra-low temperature in air via electric field assistance

Joining of SiC ceramics using the Ni-Mo filler alloy for heat exchanger applications

Brazing SiC ceramic to Zircaloy-4 using Zr-Ni filler alloy: Microstructure, mechanical properties and irradiation behavior

Reinforcement of ceramic bonded joints with intermetallic compounds