Abstract:In order to shorten construction periods, concrete is often cured using steam and is loaded at an early age. This changes the performance and even the durability of the concrete compared to concrete that has been cured under normal conditions. Thus, the pattern and the mechanism of concrete performance change under different curing conditions, and loading ages are of great significance. The development of brittleness under different curing conditions and loading ages was studied. The evaluation methods that were used to determine concrete brittleness were expounded. Steam, standard, and natural curing conditions were carried out on single-side notched concrete beams as well as on a concrete prism and cubic blocks. The compressive strength and splitting tensile strength of the concrete blocks along with the fracture performance of the concrete beams were tested after 3, 7, 28, and 90 days. The steam curing condition significantly improved the strength of concrete before 28 days had passed, and the standard curing condition improved the strength of concrete after 28 days. Based on the experimental fracture parameters, a two-parameter fracture model was applied to study the development of fracture toughness KICS, critical crack tip opening displacement CTODc, and critical strain energy release rate GICS with hydration age under different curing conditions. With respect to long-term performance, the standard curing condition was better at resisting concrete crack propagations than the steam curing condition was. The characteristic length lch and the material length Q under the three curing conditions and the long-term development of brittleness in the concrete indicated that steam curing increased the concrete brittleness. Considering the effects of the curing condition and the loading age, a time-dependent concrete fracture toughness model was established, and the predicted value of the model was verified against the measured value. The results indicated that the model was able to accurately predict the fracture toughness with an error rate of less than 16%.

Fracture Properties of Concrete in Dry Environments with Different Curing Temperatures

Experimental study on dynamic behavior of concrete at elevated temperatures

Elevated Temperature Inversion Phenomenon in Fracture Properties of Concrete and Its Application to Maturity Model

Fracture Toughness And Microstructure Of Concrete At Early-Ages

Experimental Study on the Fracture Toughness of Concrete under Different Curing Conditions

Experimental Study of Mechanical Properties of Normal-Strength Concrete Exposed to High Temperatures at an Early Age

Effect of Elevated Temperatures on Compressive Strength of Concrete

Early Age Properties and Cracking Control of Concrete

Effect of low temperatures on fracture properties of steel fibre reinforced rubberised concrete

Study on the Fracture Mechanical Properties of High Performance Concrete (HPC) with Rapid Cooling after High Temperature

Experimental Study on Some Factors Affecting Fracture Property of Concrete

Brittleness of Concrete under Different Curing Conditions

Relationship Between Characteristic Tensile Strain and Curing Age of Concrete

Effect of Temperature on Pore Structure and Strength of Concrete

The Influence of Temperatures on the Mechanical Properties and Fracture Behavior of Rocks under Mixed Mode I/II Loading

Effects of thermal treatment on the fracture behavior of rock-concrete bi-material specimens containing an interface crack

Experimental study on fracture properties of self-compacting concrete

Evaluation of Early Age Mechanical Properties of Concrete in Real Structure

Experimental Study on Mechanical Properties of Early-Aged Concrete after Exposure to High Temperatures

Dynamic Tensile Properties and Energy Dissipation of High-Strength Concrete after Exposure to Elevated Temperatures

Experimental Investigation of the Static Expansion Tensile Behavior of Concrete after Exposure to Elevated Temperatures