Abstract:Yttrium oxide doped with europium has a great prospective for FED and PDP phosphor application. In present study, the precursor of yttrium oxide hydroxide nitrate nanorod, which was prepared via hydrothermal reaction route using PEG-6000 as template from the starting Y(NO3)(3) and KOH reactant system, was used to prepare Y2O3:Eu3+ nanorod via a post annealing process during which the precursor with adjustable shape and size was transformed to final Y2O3:Eu3+ product. XRD, field emission scanning electron microscopy (FE-SEM) and photoluminescence spectra (PL) were used to characterize the crystalline, morphology and luminescence properties of as-formed Y2O3:Eu3+ products synthesized at different post annealing temperatures, respectively. The results indicate that grain morphology of obtained Y2O3:Eu3+ product was nanorod with a mean diameter of about 40 similar to 60 nm and length of about 500 similar to 700 nm, the nanorod structure and morphology of obtained Y2O3:Eu3+ product maintained during post annealing process and the size varied slightly with different annealing temperatures. Pure cubic Y2O3:Eu3+ phase was formed and the size was the smallest at annealing treatment of 500 degrees C. Under the annealing temperature below 500 degrees C its diameter increased with increasing annealing temperature, and remained in a stable size when the annealing temperature was above 500 degrees C. The PL spectra of excitation spectra of Y2O3:Eu3+ product show that it exhibits excitation band located at about 395 and 468 nm, respectively. Above two excitation bands could be ascribed to the transition 4f-4f of Eu3+ ions in the Y2O3 host. On the other hand, the main emission peaks of the as-prepared products could be ascribed to the Eu3+ ions transition from D-5(0) to F-7(2). Furthermore, the luminescent intensity was improved about three times when the annealing temperature increased from 500 to 1000 degrees C.

Preparation of Y2O3:Eu3+ Nanofibers Via Electrospinning and Study on Their Photoluminescence Properties

Fabrication and optical properties of Y2O3: Eu3+ nanofibers prepared by electrospinning.

Preparation and photoluminescence of yttrium hydroxide and yttrium oxide doped with europium nanowires

Preparation of Eu, Li co-doped ZnO red fluorescence nanofibers by electrospinning and their characterization

Preparation And Luminescence Properties Of Y2o3 : Eu3+ Nanorods Via Post Annealing Process

ELECTROSPINNING PREPARATION AND LUMINESCENE PROPERTIES OF CaTiO3: RE (Eu3+/Gd3+) NANOFIBERS

PREPARATION AND OPTICAL PROPERTIES OF CERIUM DOPED YTTRIUM ALUMINIUM GARNET NANOFIBERS BY ELECTROSPINNING

Luminescent Properties of Li+ Doped Nanosized Y2O3:Eu

Synthesis and luminescence properties of Y 2O 3:Eu with flower-like microstructure

Size-Dependent Polarized Photoluminescence From Y3al5o12: Eu3+ Single Crystalline Nanofiber Prepared By Electrospinning

SYNTHESIS OF Y_2O_3∶Eu NANOCRYSTALLINE BY COMPLEX PRECURSORS

Preparation of YIG Single Crystal Nanofibers Via an Electrospinning Technique

Preparation and characterization of rare-earth strontium aluminate luminescent nanofibers by electrospinning

White-light Emission and Weak Antiferromagnetism from Cubic Rare-Earth Oxide Eu2O3 Electrospun Nanostructures

Upconversion Luminescence of Er3+/Yb3+ Codoped NaYF4/PVP Composite Electrospun Nanofibers

Preparation, photoluminescence and photocatalytic properties of ZnO:Eu3+ nanocrystals

Hydrothermal Method Synthesis and Characterization of Yvo4:Eu3+@Ypo4 Core-Shell Phosphor

Influence of Concentration Effect and Au Coating on Photoluminescence Properties of YVO4:Eu3+Nanoparticle Colloids

Optimization of the Photoluminescence Properties of Electrodeposited Y[sub 2]o[sub 3]:Eu[sup 3+] Thin-Film Phosphors

Synthesis of Nanometer Y2o3 : Eu Phosphor and Its Luminescence Property

Two-steps Prepared Monodisperse Li-doped Y2O3:Eu3+ Microspheres and Their Luminescence Properties