Synthesis and Characterization of Thermotropic Liquid Crystalline Polyurethanes from 4,4 '-Bis(6-hydroxyhexoxy) Biphenyl and Aliphatic Diols

Chun Wei,Yongyang Gong,Xianglian Yang,Min Wang

DOI: https://doi.org/10.1002/pat.1356

IF: 3.348

2009-01-01

Polymers for Advanced Technologies

Abstract:A series of thermotropic liquid crystalline polyurethanes (LCPUs) were synthesized by the polyaddition reactions of 2,4-toluene diisocyanate (2,4-TDI) with 4,4'-bis(6-hydroxyhexoxy)biphenyl (BHHBP) and aliphatic diol. The intrinsic viscosities of the polymers were measured by Ubbelohde viscometer, and the chemical structure was confirmed by Fourier transform infrared spectroscopy (FT-IR). The LCPUs were examined by differential scanning calorimetry (DSC), polarized optical microscopy (POM), wide angle X-ray diffraction (WAXD), and thermogravimetric analysis (TGA). The intrinsic viscosities were 0.56-0.83 dl/g. According to the melting point (T(m)) and the isotropic temperature (T(i)) of the LCPUs, the temperature range of the liquid crystalline phase became wider with increased number of methylene spacers in the polyurethane. The LCPUs exhibited a nematic phase with a threaded texture and had a wide mesophase temperature range. The decomposition temperature of the LCPUs was >300 degrees C. On WAXD, the LCPUs give a dispersing peak at 2 theta approximate to 20 degrees, and a strong diffraction peak at 2 theta approximate to 25 degrees. Copyright (C) 2008 John Wiley & Sons, Ltd.