Synthesis and Thermotropic Liquid-Crystalline Behaviour of Novel Main-Chain Poly(Ether Ether Ketone Ketone)S Containing A Lateral Tert-Butyl Group

H Sun,H Na,HF Wang,WJ Zhang,ZW Wu,R Yosomiya

DOI: https://doi.org/10.1002/1097-0126(200011)49:11<1539::aid-pi494>3.0.co;2-8

IF: 3.213

2000-01-01

Polymer International

Abstract:The synthesis of novel poly(ether ether ketone ketone)s containing a lateral group via the random copolymerization of 4,4'-biphenol, tert-butylhydroquinone and 1,4-bis(p-fluorobenzoyl)benzene is described, The copolymers were characterized by differential scanning calorimetry (DSC), wide-angle X-ray diffraction (WAXD) and polarized optical microscopy (POM) observation, The results showed that the thermotropic liquid-crystalline properties were achieved in the copolymers containing 30mol% and 50mol% tert-butylhydroquinone, which have relatively lower melting temperatures due to the copolymerization effect, Both the crystalline-liquid-crystalline transition (T-m) and the liquid-crystalline-isotropic phase transition (T-i) were observable in the DSC thermograms, while the biphenol-based poly(aryl ether ketone) has only one melting transition. The hydroquinone-based polymer was shown to be amorphous. Thermogravimetric analysis (TGA) results showed that these copolymers are all high-temperature resistant with higher glass transition temperature between 147 and 149 degreesC, and higher decomposition temperature Td in the range 480-520 degreesC, (C) 2000 Society of Chemical Industry.